结合邯钢生产实践,对板坯连铸机铸坯轧后拉伸试样分层缺陷原因进行分析并提出了预防措施,有效减轻了铸坯中心偏析及疏松,提高了铸坯实物质量,减少了铸坯轧后分层缺陷。
Combining with the practice of Handan Iron and Steel Company, the cause of stratified defects in slab continuous casting slab after rolling was analyzed and preventive measures were put forward to effectively reduce the center segregation and loosening of slab, improve the physical quality of slab and reduce Slab rolling stratified defects.