The influence of Mo on the microstructure,bending strength and HV of Ti/Al 2O 3 composite was studied,and the influence mechanism was analyzed.The results indicate that after the addition of Mo,the composite organization is finer and phases distribution is better-proportioned which make the microstructure denser,the bending strength and HV of composite are also increased to a degree.But the bending strength increases first then decreases with the increasing of Mo content,so the appropriate Mo content for the Ti/Al 2O 3 composite is to be further confirmed.
The influence of Mo on the microstructure, bending strength and HV of Ti / Al 2 O 3 composite was studied, and the influence mechanism was analyzed. Results that results in the addition of Mo, the composite organization is finer and distribution of phases is better- proportioned which make the microstructure denser, the bending strength and HV of composite are also increased to a degree.But the bending strength increases first then decreases with the increasing of Mo content, so the appropriate Mo content for the Ti / Al 2O 3 composite is to be further confirmed