【摘 要】
：
模具和机械零件,在以硼砂为基体的盐浴中渗钒,能显著地提高表面硬度(HV_(0.2)22400～3400)增加耐磨性,延长使用寿命,是一般化学热处理方法不可比拟的。这种工艺方法,在国内外
【机 构】
：
北京市工程机械热处理厂,北京市工程机械热处理厂,北京市工程机械热处理厂,北京市工程机械热处理厂,北京市工程机械热处理厂
论文部分内容阅读
模具和机械零件,在以硼砂为基体的盐浴中渗钒,能显著地提高表面硬度(HV_(0.2)22400～3400)增加耐磨性,延长使用寿命,是一般化学热处理方法不可比拟的。这种工艺方法,在国内外已成功地应用于铁基合金模具上。我们对40Cr、45、GCr15和T10钢进行硼砂五氧化二钒盐浴表面渗钒研究,并在此基础上,对GCr15钢锥阀进行表面渗钒试验,取得了明显效果。
It is incomparable to the general chemical heat treatment method that the vanadium is infiltrated into the salt bath with borax as the base, and the surface hardness (HV 0.22400 ~ 3400) can be remarkably increased by increasing the wear resistance and prolonging the service life of the mold and the mechanical parts. This process has been successfully applied to iron-based alloy molds at home and abroad. On 40Cr, 45, GCr15 and T10 steel we vanadium infiltration vanadium salt bath surface vanadium penetration, and on this basis, GCr15 steel cone valve on the surface of vanadium penetration test, and achieved significant results.
其他文献
一、前言 众所周知,钢铁材料是一种具有多型性转变的金属,其内部组织中存在各种不同的组成相,钢铁材料的性能决定于这些相的组成。因此,分析钢铁材料内部的组织组成;研究各
本文首先介绍了Jaeger 的移动热源热模型图,切断磨削热模型图和蠕动进给磨削热模型图。在此基础上论述了高效率成型磨削时的热源分布与热传导情况。由于磨削时的热损伤引起
机械压力机是除锻锤外会产生明显振动的另一类锻压机械.在速度较低、吨位不大的情况下,压机振动的后果还不太引人注意,但是当压机的速度和吨位超过一定限度时,振动问题就会
跳过陈旧的训练计划,使用一种全新的方式来塑造一个可靠的背部和超强的肱二头肌。
Skip outdated training plans and use a whole new way to create a solid back and sup
想去健身?没问题!想享受豪华却不奢华的礼遇,心情愉快地健身?也没问题!前提是你得选对地方。想象一下:在昏暗的灯光下抓起哑铃、在人声嘈杂的环境中憋着劲流汗、等待占用器械
本文利用扫描电镜对高比重W-Ni-Cu合金在压弯破断过程中裂纹的发生、发展进行了观察。在此基础上,对断裂过程进行了讨论。
In this paper, the occurrence and development
文中介绍了在恒压力和恒进给条件下,刚玉砂带和锆刚玉砂带的磨损特征和磨削性能。
In this paper, wear characteristics and grinding performance of corundum and zircon
大连地区冬季气温平均在零下2℃左右,相对于哈尔滨的深寒,可算是“东北的江南”。从2003年以来,大连陆续开办了4家大型滑雪场,如安波滑雪场、林海滑雪场、铭湖滑雪场和欢乐雪
我们习惯叫他老费,“老”是因为在经常打球的这帮朋友里,他岁数最大;“费”当然是因为姓费,还有一个原因就是他无限崇拜德勒。
We used to call him the old fee, “old ”
论述了英文歌曲作为英语教学的辅助手段,在大学英语精读、听力教学中的运用.
It discusses the application of English songs in English intensive reading and listening