【摘 要】
：
Porous TiAl3 intermetallics were fabricated through vacuum reactive sintering from Ti-75Al at.％ elemental powder mixture.The phase compositions,expansion behaviors,pore characteristics and microstructure evolution of TiAl3 intermetallics were investigated
【机 构】
：
School of Materials Science and Engineering, China University of Mining and Technology, Xuzhou 22111
论文部分内容阅读
Porous TiAl3 intermetallics were fabricated through vacuum reactive sintering from Ti-75Al at.％ elemental powder mixture.The phase compositions,expansion behaviors,pore characteristics and microstructure evolution of TiAl3 intermetallics were investigated,and the pore formation mechanism was also proposed.It was found that the actual temperature of compacts showed an acute climb from 668 to 1244 ℃ in 166s,while the furnace temperature maintained the linear growth of 5 ℃/min,which indicated that an obvious thermal explosion (TE) reaction occurred during sintering,and only single-phase TiAl3 intermetallic was synthesized in TE products.The open porosity increased from 22.2 (green compact) to 32.8％ after reactive diffusion sintering at 600 ℃ and rised to 58.7％ after TE,then decreased to 51.2％ after high-temperature homogenization at 1100 ℃.Therefore,TE reaction is the dominated pore formation mechanism of porous TiAl3 intermetallics.The pore evolution in porous TiAl3 intermetallics occurred by the following mechanisms:certain intergranular pores remained among powder particles of green compact,then low-temperature sintering resulted in a further increase in porosity due to the Kirkendall effect.Moreover,TE reaction gave rise to a dramatic volume expansion because of the rapid increase in temperature,and high-temperature sintering caused densification and a slight shrinkage.
其他文献
In this work,the corrosion behaviours of the amorphous Ni84.9Cr7.4Si4.2Fe3.5 alloy and its crystalline counterpart are studied in acidic,neutral,and alkaline solutions by scanning electron microscopy,electrochemical impedance spectroscopy,and potentiodyna
Anisotropic SmCo5/Co nanocomposite powders have been prepared by electroless Co deposition on commercial SmCo5 powders with hydrazine as reducer.The Co particles are mainly in the range of 8-27 nm and form dense/continuous soft magnetic coatings on the su
The effects of ausforming procedure and subsequent annealing treatments on microstructures of cobalt (Co) samples are investigated by electron channeling contrast and electron backscatter diffraction techniques.Results show that the ausformed Co samples c
Hybrid aluminum matrix composite powders reinforced with bimodal-sized Al2O3 particles were synthesized by mechanical milling.Two different approaches were investigated for the addition of submicron-and nano-sized Al2O3 particles to the aluminum powders.I
Hot compression tests were carried out with specimens of 20Cr-24Ni-6Mo super-austenitic stainless steel at strain rate from 0.01 to 10 s-1 in the temperature range from 950 to 1150 ℃,and flow behavior was analyzed.Microstructure analysis indicated that dy
In this work,surface characterization and electrochemical measurement were employed to investigate the effects of magnetic field (MF) on the corrosion of Q235 carbon steel in a NaCl solution containing sulphate-reducing bacteria (SRB) or extracellular pol
The hot deformation behavior of a medium-Mn steel was studied in terms of hot compression flow curves in the temperature range of 850-1050 ℃ and strain rates of 0.05-10 s-1.The thermo-mechanical analysis was carried out and suggested that the microstructu
Corrosion inhibition of tolytriazole for galvanized steel was studied in 5 mM NaCl by using potentiodynamic polarization and electrochemical impedance spectroscopy (EIS),scanning vibrating electrode technique (SVET).The results of EIS and polarization tes
In this work, a series of biodegradable pure iron, Fe-30Mn and Fe-30Mn-Ag alloys were developed by using a rapid solidification technology. A fine α-Fe dendrite was formed in pure iron, resulting in a high compressive yield strength of above 300 MPa. The
In this study, Al-Zn and Al-Mg coatings were deposited on steel substrates by an arc thermal spray process. X-ray diffraction and scanning electron microscopy were used to characterize the deposited coatings and corrosion products. Open circuit potential