【摘 要】
：
Sandwich-like Al/Ti/Al-laminated composites have many advantages such as low density and high specific strength with value in mechanical manufacturing and aerospace engineering.Here,Al/Ti/Al-laminated composites were fabricated by hot roll bonding and sub
【机 构】
：
State Key Laboratory of High Performance Complex Manufacturing, Central South University, Changsha 4
论文部分内容阅读
Sandwich-like Al/Ti/Al-laminated composites have many advantages such as low density and high specific strength with value in mechanical manufacturing and aerospace engineering.Here,Al/Ti/Al-laminated composites were fabricated by hot roll bonding and subsequent processes: cryorolling (-190 ℃ and-100 ℃),cold rolling (25 ℃),and hot rolling (300 ℃).Their bonding strength and mechanical properties were then studied by an Autograph AGS-X universal electronic testing machine.The results show that cryorolling can improve the interface bonding strength and tensile strength of Al/Ti/Al-laminated composites.For the Al/Ti/Al-laminated composites subjected to cryorolling at-100 ℃,they have the highest strength near 260 MPa-this is 48 MPa and 41 MPa higher than the laminated composites subjected to cold and hot rolling,respectively.These results also show the strongest peeling strength.Finally,the mechanisms of the enhancement of bonding strength and mechanical properties of Al/Ti/Al-laminated composites subjected to cryorolling were mainly discussed.
其他文献
Fe-10 at.％Cr alloy was implanted with hydrogen ions at room temperature,followed by annealing at high temperatures.The annealing process made the defects develop into large dislocation loops.The nature of the dislocation loops formed after annealing was s
The work is mainly to study the thermal stability including the phase stability,microstructure and tribo-mechanical properties of the A1B2-type WB2 and W-B-N (5.6 at.％ N) films annealed in vacuum at various temperatures,which are deposited on Si and GY8 s
The dynamic mechanical relaxation behavior of Ti36.2Zr30.3Cu8.3Fe4Be21.2 bulk metallic glass with good glass-forming ability was investigated by mechanical spectroscopy.The mechanical relaxation behavior was analyzed in the framework of quasi-point defect
CoFe2O4 nanoparticles (NPs) and surface modified with gold (Au) have been synthesized by a thermal decomposition method.The obtained NPs and formation of CoFe2O4@Au core-shell (CS) were confirmed by characterizing their structural and optical properties u
Plasma nitriding is a widely used technology to enhance the surface performance and extend the service life of alloy parts.The current research mainly focuses on the influences of time,temperature,gas type and pressure parameters on nitriding behavior,whi
This paper clarifies two issues related to the prior cathodic polarisation treatment (PCPT) for the potentiodynamic polarisation test: whether PCPT can (1) remove the air-formed surface film and (2) affect the polarisation test results.X-ray photoelectron
A new method for evaluating the compactness of rust layers on steels has been proposed in the present study.The method includes adsorption and dehydration process of anhydrous ethanol.The protective ability of rust layers can be qualitatively reflected by
Electron diffraction was used to study the local atomic structure of Cu49Hf42Al9 metallic glasses (MGs).The amorphous nature of the MG was fully retained after the compression test.The partial radial distribution functions (PRDFs) of the MG structure obta
The effect of grain size on the mechanical properties of a high-manganese (Mn) austenitic steel was investigated via electron-backscattered diffraction,transmission electron microscope,X-ray diffraction,and tensile and impact tests at 25 ℃ and-196 ℃.The H