【摘 要】
：
The work is mainly to study the thermal stability including the phase stability,microstructure and tribo-mechanical properties of the A1B2-type WB2 and W-B-N (5.6 at.％ N) films annealed in vacuum at various temperatures,which are deposited on Si and GY8 s
【机 构】
：
College of Materials Science and Engineering, Xi’an Shiyou University, Xi’an 710065, China;Institute
论文部分内容阅读
The work is mainly to study the thermal stability including the phase stability,microstructure and tribo-mechanical properties of the A1B2-type WB2 and W-B-N (5.6 at.％ N) films annealed in vacuum at various temperatures,which are deposited on Si and GY8 substrates by magnetron sputtering.For the WB2 and W-B-N films deposited on Si wafers,as the annealing temperature increases from 700 to 1000 ℃,a-WB (700 ℃) and Mo2B5-type WB2 (1000 ℃) are successively observed in the AlB2-type WB2 films,which show many cracks at the temperature ≥ 800 ℃ resulting in the performance failure;by contrast,only slight α-WB is observed at 1000 ℃ in the W-B-N films due to the stabilization effect of a-BN phase,and the hardness increases to 34.1 GPa first due to the improved crystallinity and then decreases to 31.5 GPa ascribed to the formation of α-WB.For the WB2 and the W-B-N films deposited on WC-Co substrates,both the WB2 and W-B-N films react with the YG8 (WC-Co) substrates leading to the formation of CoWB,CoW2B2 and CoW3B3 with the annealing temperature increasing to 900 ℃;a large number of linear cracks occur on the surface of these two films annealed at ≥ 800 ℃ leading to the film failure;after vacuum annealing at 700 ℃,the friction performance of the W-B-N films is higher than that of the deposited W-B-N films,while the wear resistance of the WB2 films shows a slight decrease compared with that of the deposited WB2 films.
其他文献
The cooling curves and the change of contraction/expansion during solidification and cooling were tested by using a selfmade device which could achieve the one-dimensional contraction instead of three-dimensional contraction of the casting.Then,the effect
The microstructure and mechanical properties of the as-cast and heat-treated Mg-4.6Y-2.5Zn-0.6Zr-xSn (x =0,0.2 and 0.5 wt％) alloys were investigated in this work.The results showed that the eutectics have been refined with 0.2％ Sn addition and it has no e
Previous studies showed that significant increases in elongation in Mg-Ce alloys due to the Ce addition and the solute drag effect by Ce addition were ascribed to the non-basal dislocation slip activating and the texture altering.The microstructure evolut
The Mg MB26/Al 7075 composite rod,in which Mg MB26 serves as the sleeve and Al 7075 serves as the core,is fabricated via the process of co-extrusion.The influence of extrusion speed on the microstructure evolution,interface bonding and mechanical response
Aiming at the requirements of structural steel in Gen-IV nuclear reactor,the high-chromium martensitic heat-resistant steels containing 10-12％ chromium were developed.The toughness of heat-affected zones (HAZs) is one of the important factors for evaluati
In the present study,the weld formation and mechanical properties of the AA-5A06 friction pull plug welded (FPPW) joints were improved by controlling the axial force history.Several defect-free FPPW joints were made successfully by using the welding param
A 17 vol％ SiCp/Al-Mg-Si-Cu composite plate with a thickness of 3 mm was successfully friction stir welded (FSWed) at a very high welding speed of 2000 mm/min for the first time.Microstructural observation indicated that the coarsening of the precipitates
In the present experimental investigation,Al-3 wt％Cu and A1-3 wt％Cu-0.5 wt％Mg alloys castings are produced by a horizontal solidification technique with a view to examining the interrelationship among growth rate (GR),cooling rate (CR),secondary dendrite
In this study,near fully dense (96.5％) pure tungsten bulks were additively manufactured and the cracking behavior was investigated.A crack network with a spacing of ～ 100 μm was observed in the fabricated bulks.It was observed that the laser scanning stra
Fe-10 at.％Cr alloy was implanted with hydrogen ions at room temperature,followed by annealing at high temperatures.The annealing process made the defects develop into large dislocation loops.The nature of the dislocation loops formed after annealing was s