采用电沉积法将Ｔｅ电沉积在以Ｎｉ为底衬的Ｃｕ靶托上，制备出了质子回旋加速器ＣＹＣＬＯＮＥ－３０用碲靶，用以生产放射性医用同位素１２３Ｉ。研究了电流密度、电沉积时间、温度、电沉积溶液中碲的质量浓度（以ＴｅＯ２计）、碱度等工艺条件对碲靶质量的影响。推荐最佳工艺条件为：电沉积液介质浓度ｃ（ＫＯＨ）＝１ｍｏｌ／ｌ；ρ（ＴｅＯ２＝５５－６５ｍｇ／ｍｌ；电流密度Ｊ＝１０－１２ＭＡ／ｃｍ２；温度Ｔ＝１８－３０℃；电沉积时间ｔ约为１ｈ。在此工艺条件下制备的碲靶的质量厚度为１４－２０ｍｇ／ｃｍ２，沉积层质地致密、均匀、无斑点，附着力强。
Electrodeposition of Te electrodeposited on the Ni-based Cu target support prepared proton cyclotron CYCLONE-30 with a tellurium target, used to produce radioactive isotope 123I. The effects of current density, electrodeposition time, temperature, concentration of tellurium in electrodeposition solution (calculated as TeO2) and alkalinity on the quality of tellurium target were studied. The optimum process conditions are as follows: concentration of electrodeposition solution c (KOH) = 1mol / l; ρ (TeO2 = 55-65mg / ml; current density J = 10-12MA / cm2; temperature T = 18-30 ℃; The deposition time t is about 1 h.The quality of the tellurium target prepared under this process condition is 14-20 mg / cm 2, the deposited layer is dense, uniform, without spots and strong adhesion.