论文部分内容阅读
Electrodeposition technique was used to coat calcium phosphate on carbon fiber which can be used to reinforce hydroxyapatite. The differences between fibers treated with and without nitric acid in electrodeposition were evaluated. The X-ray diffractometry results show that CaHPO_4·2H_2O is obtained as the kind of calcium phosphate coating on carbon fiber. The scanning electron microscopy photographs and deposit kinetic curve indicate that the influences of the functional group attained by nitric acid treatment, the crystal morphology and crystallization of the coating layers on the fiber with and without treatment rate are obviously different. The functional group, especially the acidic group, can act as nucleation centers of electrochemical crystallization.
The differences between fibers treated with and without nitric acid in electrodeposition were evaluated. The X-ray diffractometry results show that CaHPO_4 · 2H_2O is obtained as the kind of the kind of coated calcium phosphate on carbon fiber which can be used to reinforce hydroxyapatite. of calcium phosphate coating on carbon fiber. The scanning electron microscopy photographs and deposit kinetic curve that that the influences of the functional group attained by nitric acid treatment, the crystal morphology and crystallization of the coating layers on the fiber with and without treatment rates are obviously different. The functional group, especially the acidic group, can act as nucleation centers of electrochemical crystallization.