This paper studies the effect of oxygen partial pressure on the fabrication of YBa 2 Cu 3 O 7 x films on (00l) LaAlO 3 substrates by metalorganic deposition using trifluoroacetates (TFA-MOD).As the oxygen partial pressure increases to 1500 Pa,a great increase in the superconducting properties is observed at high magnetic fields parallel to the YBCO c axis.The cross-sectional transmission electron microscope images show that a high density of stacking faults in the size range of 10-15 nm may act as flux pinning centres to enhance the critical current density of the YBCO films
This paper studies the effect of oxygen partial pressure on the fabrication of YBa 2 Cu 3 O 7 x films on (00l) LaAlO 3 substrates by metalorganic deposition using trifluoroacetates (TFA-MOD). As the oxygen partial pressure increases to 1500 Pa, a great increase in the superconducting properties is observed at high magnetic fields parallel to the YBCO c axis. cross-sectional transmission electron microscopy images show that a high density of stacking faults in the size range of 10-15 nm may act as flux pinning centers to enhance the critical current density of the YBCO films