原始青瓷是瓷器原始阶段时的制品,一般认为产生于商周时期。原始青瓷的胎体用瓷土作原料,含铁量在2%左右,经过人工施釉,在1200℃左右的高温中烧成。器物大多为罐、碗、盘、豆等日用器,也有仿青铜器的尊、卣、簋、鼎等器型。春秋、战国时也有一部分钟、于等仿青铜乐器。原始青瓷在中国南方、北方均有发现,尤其以浙江北部、江苏南部太湖地区的吴越故土最为集中。经化验后证明,这些原始青瓷的瓷胎系用瓷土烧制而成,其釉是以铁的氧化物为着色剂的高温釉,釉色以青
The original celadon porcelain is the original stage of the product, generally believed to have originated in Shang and Zhou dynasties. The original celadon carcasses with porcelain as raw materials, iron content of about 2%, after artificial glazing, firing at about 1200 ℃ in high temperature. Utensils mostly for cans, bowls, plates, beans and other daily appliances, there are imitation bronze respect, 卣, 簋, Ding and other types. Spring and Autumn Period, the Warring States period also has a part of the clock, such as imitation bronze instruments. The original celadon was found in southern China and the north, especially in the northern part of Zhejiang Province and in the Taihu Lake in southern Jiangsu. After the test proved that these primitive celadon porcelain fetal system firing with clay, the glaze is iron oxide as a coloring agent of high temperature glaze, glaze to green