Al2O3 porous nanosolid was prepared via solvothermal hot-press(SHP) method.The dielectric constant of Al2O3 porous nanosolid is as low as 2.34,while its compressive strength is very poor.In order to improve the compressive strength and maitain low dielectric constant,polyimide was introduced to prepare Al2O3 /polyimide composite porous nanosolid.Compared to Al2O3 porous nanosolid,Al2O3 /polyimide composite porous nanosolid possesses much higher compressive strength,which reaches its saturation value when the mass loading of polyimide is 7.75%.In addition,the in situ Fourier transformation infrared(FTIR) monitoring result reveals that Al2O3 /polyimide composite porous nanosolid is stable up to 400 °C.
Al2O3 porous nanosolid was prepared via solvothermal hot-press (SHP) method. The dielectric constant of Al2O3 porous nanosolid is as low as 2.34, while its compressive strength is very poor. In order to improve the compressive strength and maitain low dielectric constant, was introduced to prepare Al2O3 / polyimide composite porous nanosolid. Compared to Al2O3 porous nanosolid, Al2O3 / polyimide composite porous nanosolid possesses much higher compressive strength, which reaches its saturation value when the mass loading of polyimide is 7.75% .In addition, the in situ Fourier transformation infrared (FTIR) monitoring results in that Al2O3 / polyimide composite porous nanosolid is stable up to 400 ° C.