采用Al+Nb对Ti-6Al-4V进行激光表面合金化处理,在适当的工艺参数下,得到了TiAl3+TiAl+少量Al的合金化层,在900℃空气介质中的氧化试验结果表明,激光合金化层在氧化时能够形成致密、连续的α-Al2O3保护膜层,对基体起到了良好的抗氧化保护作用
TiAl3 + TiAl + Al alloy layers were obtained by laser surface alloying Al-Nb with TiAl3 + TiAl + under appropriate process parameters. The results of oxidation experiments in air at 900 ℃ showed that the laser alloying layer was oxidized Can form a dense, continuous α-Al2O3 protective film, the substrate has played a good antioxidant protection