制备Mg-2.5wt%Zn和Mg-2.5wt%Zn-0.5wt%Zr合金,对其微观组织、力学性能和体外降解行为进行对比。结果表明,Zr元素对Mg-Zn合金的细化作用显著,合金的晶粒尺寸由60μm减小到20μ
【机 构】
：
天津理工大学材料科学与工程学院,天津市光电显示材料与器件重点实验室,显示材料与光电器件省部共建教育部重点实验室,
论文部分内容阅读
制备Mg-2.5wt%Zn和Mg-2.5wt%Zn-0.5wt%Zr合金,对其微观组织、力学性能和体外降解行为进行对比。结果表明,Zr元素对Mg-Zn合金的细化作用显著,合金的晶粒尺寸由60μm减小到20μm。添加Zr使Mg-Zn合金的强度、塑性和硬度均有所提高,其抗拉强度和伸长率分别达到315 MPa和21.4%。经体外降解测试,Mg-2.5wt%Zn-0.5wt%Zr合金的平均降解速率为3.32 mm/a,其耐蚀性优于Mg-2.5wt%Zn合金。
Preparation of Mg-2.5wt% Zn and Mg-2.5wt% Zn-0.5wt% Zr alloy microstructure, mechanical properties and in vitro degradation behavior were compared. The results show that the refining effect of Zr on the Mg-Zn alloy is remarkable. The grain size of the alloy is reduced from 60μm to 20μm. Addition of Zr enhanced the strength, ductility and hardness of Mg-Zn alloy, and its tensile strength and elongation reached 315 MPa and 21.4% respectively. The degradation rate of Mg-2.5wt% Zn-0.5wt% Zr alloy was 3.32 mm / a and its corrosion resistance was better than that of Mg-2.5wt% Zn alloy.
其他文献
人们在谈论戏曲的危机问题时，大都关注在戏曲的内容、形式、创新等问题上，我想，如果戏曲没有了教育家，那将是严重的危机。如何出现更多的戏曲教育家，这是一个很值得研究的问题。我
没人知道陕西榆林孕妇马茸茸经历了多大的痛苦,才最终选择纵身一跃结束了一切。那么,生孩子到底是一种怎样的人生体验?分娩到底有多疼?无痛分娩是不是就真的不痛了呢?生孩子
《珍珠烈火旗》是当年王瑶卿先生的拿手好戏。这出戏唱、做、念、打繁重，根据我的记忆这出戏只教过几个男学生，仅有宋德珠在中华戏校时演出过，宋饰双阳公主、李德斌扮演狄青。建
目的:探讨胎心监测联合脐血流S/D检测对胎儿窘迫的预测价值。方法:选择2011年4月-2016年4月我院的100例足月孕妇,将其分为对照组和观察组,每组50例。对照组采用胎心监测,观察
严格地讲,２７集电视连续剧《永不瞑目》骨子里不能算是公安题材电视剧,因为片中的男主人公不是公安民警,而是一个正在学校就读的大学生肖童。他年轻、英姿勃发、上进、不愁衣食,
目的 :研究剖宫产术中产后出血应用B-Lynch缝合术进行治疗的效果。方法 :选取我院2014年3月到2016年9月期间于我院妇产科行剖宫产,并且因宫缩乏力而出现产后出血的产妇120例
机关党委要为全委的青年干部创造更多相互学习和交流平台,推动青年干部的管理经验共享,促进青年干部管理能力的提高。要根据机关党委的安排,扎实推进“司局长谈培养青年”活
知名的企业需要知名的品牌，知名的品牌是由可信赖的产品与时间的累积所创造的。而品牌一旦深入人心，便会与市场营销、经济效益产生互映互动的联系。许多有远见、有抱负的企业家
随着国民经济的高速发展 ,我国文娱产业已进入蓬勃发展的阶段 ,这一产业的许多领域需使用民用（甚至军用）早已沿用很久的技术标准 ,例如舞台机械密切相关的剧场建筑设计规范 ,与
8月 3日至 5日北京举办了“中美电影电视高级研讨会”。这次会议是经国家广播电影电视总局批准 ,由中国电影电视技术学会、北京紫禁城影业公司、北京海外广播影视交流中心与