The microstructure of semi-solid slurry of AZ91D alloy, which was produced by twin-screw stirring mixer under the different parameters, was investigated.Rheoforming by cold chamber die casting process was performed thereafter. The results indicate that with decreasing of the barrel temperature of the mixer and the pouring temperature of molten Mg alloy, the solid fraction of semi-solid slurry increases and the size of non-dendritic grains becomes smaller. While the shear rate increases, the solid fraction of semi-solid slurry decreases. The tensile strength and elongation of metal rheoformed by die casting are higher by about 37% and 44% respectively than those produced by conventional liquid die casting.
The microstructure of semi-solid slurry of AZ91D alloy, which was produced by twin-screw stirring mixer under the different parameters, was investigated. Rheoforming by cold chamber die casting process accomplished thereafter. The results indicate that with decreasing of barrel temperature of the mixer and the pouring temperature of molten Mg alloy, the solid fraction of semi-solid slurry increases and the size of non-dendritic grains becomes smaller. While the shear rate increases, the solid fraction of semi-solid slurry decreases. and elongation of metal rheoformed by die casting are higher by about 37% and 44% respectively than produced produced by conventional liquid die casting.