论文部分内容阅读
在过去的报导中,曾简要地评论过合金的研究方向,那就是要合成具有高热稳定性、特殊的机械性能以及成本适当的金属玻璃。钼基金属玻璃就是其中的几个,它具有高结晶温度(Tc≥800℃)和高硬度(Hv≥1600kg/mm~2)的良好结合。正如我们所熟知的大多数非金属玻璃一样,它们要掺合大量的非金属成份(约20%),目的是使其成为玻璃态的物质。然而,实验证明,把如此高的非金属含量与大量的高熔点元素混合在一起,常常会导致淬火后玻璃态的脆性增加。随后的研制方案,试图从改善合金的成份着手,以便在与早期生产的铁基和非铁基玻璃相当的水准上
In the past reports, we briefly reviewed the research direction of alloys, which is to synthesize metallic glass with high thermal stability, special mechanical properties and reasonable cost. Molybdenum-based metallic glass is one of several, which has a good combination of high crystallization temperature (Tc ≥ 800 ℃) and high hardness (Hv ≥ 1600kg / mm ~ 2). Like most non-metallic glasses we know, they are blended with a large amount of non-metallic ingredients (about 20%) in order to make them glassy. However, experiments have shown that mixing such a high nonmetal content with a large amount of high melting point elements often leads to an increase in the brittleness of the glass state after quenching. Subsequent development programs, trying to improve the composition of the alloy to start in order to early production of iron-based and non-iron-based glass on the same level