论文部分内容阅读
A series of poly( N-isopropyl acrylamide) (PNIPAM) samples with molecular weight ranging from 2.23×10~4 to 130×10~4 and molecular weight distribution M_w/M_n≤1.28 were obtained by free radical polymerization and repeat precipitation fractionation. The molecular weight M_w, second virial coefficient A_2 as well as the mean-square-root radius of gyration 〈S~2〉 for PNIPAM samples in tetrahydrofuran (THF) were determined by light scattering, and the relations were estimated at A_2 ∞ M_w~0.25) and 〈S~2〉~(1/2)=1.56×10~(-9) M_w~(0.56). The intrinsic viscosity for THF solution and methanol solution of PNIPAM samples was measured and the Mark-Houwink equations were obtained as [η]=6.90×10~(-5) M~(0/73) (THF solution) and [η]=1.07×10~(-4) M~(0.71) (methanol solution). The above results indicate that both THF and methanol are good solvents for PNIPAM. The limit characteristic ratio C_∞ for PNIPAM in the two solutions was determined to be 10.6 by using Kurata-Stockmayer equation, indicating that the f