【摘 要】
：
本文研究了单向纤维增强复合材料的热膨胀性能。引进界面粘结系数C,利用热弹性理论推导出经C修正后的线膨胀系数计算公式。由MOM型综合热分析仪测量了玻璃纤维和碳纤维复合材
论文部分内容阅读
本文研究了单向纤维增强复合材料的热膨胀性能。引进界面粘结系数C,利用热弹性理论推导出经C修正后的线膨胀系数计算公式。由MOM型综合热分析仪测量了玻璃纤维和碳纤维复合材料在不同界面情况及不同纤维体积含量时的线膨胀系数。理论计算值与实测值相当接近,相对误差小于10％。
This article studies the thermal expansion properties of unidirectional fiber-reinforced composites. The interfacial adhesion coefficient C is introduced, and the formula for calculating the coefficient of linear expansion after C correction is derived from the thermoelastic theory. The linear expansion coefficient of glass fiber and carbon fiber composite at different interface conditions and different fiber volume contents was measured by MOM comprehensive thermal analyzer. Theoretical and measured values are quite close, the relative error is less than 10%.
其他文献
由于量块在长度计量中普遍应用和频繁使用,往往会产生锈迹、划痕、碰点、毛刺等,导致研合性差等缺陷。在检定中,为了使量块准确度等级满足规程和工作需要,必须对量块进行修理
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
本文首先阐述了吸波体的反射系数对吸波材料电磁参数的依赖关系,然后详细论述了材料的电磁参数对成分和制备工艺的依赖关系,最后介绍锂系铁氧体材料的一些实验结果。
In thi
本文综述了1970年至1984年碳-碳复合材料的主要文献,评述了工艺技术、材料性能及应用现状。分析了碳-碳复合材料的发展趋势。
This paper reviews the main literature of c
本文用X射线衍射、热学分析、磁性测量等手段研究了Nd-Fe-B(B≤50at.％)三元系相图,主要结果如下:1.重新测定了Nd-Fe二元系相图,确证NdFe_2相是不存在的。2.测定了Nd-Fe-B(B≤5
本文简要地回顾了拉挤成形工艺(以下简称拉挤工艺)的发展历史和现状;较为详细地谈到了拉挤成型的玻璃钢和碳纤维复合材料制品的应用、成型工艺和原材料问题,也谈到了今后的发
配制了38种复杂成分镍基实验合金,测定其γ′固溶温度,利用回归分析方法确定了γ′固溶温度和合金元素间的定量关系并对合金元素的影响进行了评论。用所得的γ′固溶温度线性
本文用短路开路法在8～12.4GHz频率范围内,对有机导电高聚物的微波吸收特性与掺杂剂的性质、室温电导率和试样厚度等参量的关系进行了研究。实验结果表明:当导电聚合物的电导率
一、表面改性的意义及作用广义而言,表面改性就是通过某种工艺手段使固体(主要指金属)的表面具有不同于基体材料的组织结构、化学组成,因而具有不同于基体材料的性能。经过
“材料设计”的说法始于五十年代中期,近年来逐渐形成潮流,亦已引起我国科学界和工程界的关注。我们从事与材料设计有关的研究已多年,现谨将有关情况作一综述,以供参考。一