We investigated the effects of Al concentration on the reciprocated motion of twin boundaries in pre-strained Mg-Al-Zn alloys through a combination of applied compression and tension,in-situ electron-backscattering diffraction observations,and high-angle annular dark-field scanning transmission electron microscopy observations.The twin growth was restricted by increased Al concentration,which resulted in the occurrence of smaller-sized twins.The reverse motion of twin boundaries was also restricted,resulting in the formation of higher fractions of secondary twins and 2-5° boundaries during reverse tension.The secondary twins and 2-5° boundaries mainly contributed to the increased ultimate tensile strength of the pre-strained Mg alloys.This effect is more significant in Mg alloys with larger pre-compression.Moreover,the increased amount of the Al solute atoms,rather than the precipitates,mainly contributed to the increased strengthening effect on the twin boundary motion.Our research contributes to development of high-strength Mg alloys by stabilizing twin boundaries.