One step method of structure engineering porous graphitic carbon nitride for efficient visible-light

来源 :材料科学技术(英文版) | 被引量 : 0次 | 上传用户:limiao912
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
Porous g-C3N4 nanosheets (PCN) were prepared by the nickel-assisted one-step thermal polymerization method.Hydrogen (H2) which was produced by the reaction between nickel (Ni) foam and ammonia (NH3) defined the structure and properties of PCN.During the formation of PCN,the participation of H2 not only enhanced the spacing between layers but also boosted the specific surface area that more active sites were exposed.Additionally,H2 promoted pores formation in the nanosheets,which was beneficial to the transfer of photons through lamellar structure and improved the absorption efficiency of visible light.Remarkably,the obtained PCN possessed better Cr(Ⅵ) photocatalytic reduction efficiency than pure g-C3N4.The reaction rate constant (k) of PCN (0.013 min-1) was approximately twice that of bare g-C3N4 (0.007 min-1).Furthermore,the effects of original pH and concentration of Cr(Ⅵ)-containing solution on removal efficiency of Cr(Ⅵ) were explored.A possible photocatalytic mechanism was proposed based on the experiments of radical scavengers and photoelectrochemical characterizations.
其他文献
针对印刷板式换热器换热板片表面缺陷的尺度问题,开展试验分析研究,重点研究了板片表面缺陷宽度对换热器芯体扩散焊性能的影响规律,从拉伸强度和微观界面组织两个方面阐述了
By a combination of the nanoindentation and electron probe microanalysis (EPMA) techniques,the traditional diffusion couple technique is extended to map the mec
Developing low-cost,efficient,and stable non-precious-metal electrocatalysts with controlled crystal structure,morphology and compositions are highly desirable
采用有限元辅助进行碳纤维扭转轴定刚度设计,通过碳纤维缠绕成型工艺制备碳纤维扭转轴,并进行扭转刚度测试验证.结果 表明,有限元计算得到碳纤维扭转轴扭转刚度为31.08 kN·m
针对目前模压、缠绕等工艺成型烧蚀防热复合材料易造成层间结合差、脱粘、抗烧蚀性能差、易剥蚀等问题,提出了一种新型压力辅助RTM工艺,并对其进行了树脂充模流动模拟,制备了烧蚀防热复合材料,测试了材料的孔隙率、力学性能、烧蚀性能。结果表明:压力辅助RTM工艺具有可行性与优越性,复合材料孔隙率4.64%,层间剪切强度39.3 MPa,线烧蚀率0.017 mm/s,质量烧蚀率0.0538 g/s。说明压力辅助RTM工艺适合成型烧蚀防热复合材料。
梳理和分析了水下阀门的设计规范、选材原则、设计要求、性能考核要求等,为水下阀门的工程化研制提供技术支持和研究依据。
金属材料疲劳裂纹扩展速率是对金属材料及其零构件含有裂纹体后安全服役评价及疲劳寿命评估的一项重要力学性能指标。基于金属材料疲劳裂纹扩展过程的不同阶段、闭合效应、应力比对疲劳裂纹扩展速率的影响等多个方面,对几种常见金属材料疲劳裂纹扩展速率模型的应用特点进行了对比分析,为安全设计及寿命评估时不同模型的选择应用提供参考。
Ultrafine-grained alloys fabricated by severe plastic deformation (SPD) have high strength but often poor uniform ductility.SPD via high-ratio differential spee
The widespread use of water-repellent superhydrophobic surfaces is limited by the inherent fragility of their micro-and nanoscale roughness,which is prone to da
Super-fine L10-FePt nanoparticles (NPs) with high ordering degree were successfully prepared by a modified two-step sintering method,which includes low-temperat