The influence of homogenization conditions on microstructures of AA8021 aluminium foil stock was investigated by Optical Microscope (OM), Sigmatest eddy current instrument and Quantitative Metallography Analysis (QMA) technology.The results show that grain structure of foil stock without homogenization is partial recrystallization, and the microstructure is rolling structure near plate surface after intermediate annealing.

其他文献

Effect of solute elements on strengthening and work hardening of aluminium alloys at various tempera

This work is an experimental study on solid solution strengthening of aluminium alloys.Flow behaviour of high-purity Al-Mg and Al-Si binary alloys is characterised and compared to that of a base mater

会议

The solid solution hardening of Mg in Al-Mn-Cu brazing sheet alloys at the room and elevated tempera

Al-1.5％Mn-0.5％Cu alloys with increasing Mg content from 0.1, 0.5, 1.0, 1.5 to 2.0wt.％have been developed for automotive heat exchanger units.They were DC cast and processed down to a final gauge of 1m

会议

Assessment of deformation behavior in aluminum alloy with diffraction-amalgamated grain-boundary tra

The behavior of individual grain during plastic deformation is affected by shape and size of grains and the crystal orientations for the grains in polycrystalline.We proposed new diffraction-amalgamat

会议

Microstructural evolution in an Al-Mg-Er alloy during fatigue deformation

Precipitate strengthening is a major strengthening mechanism for aluminum alloys, and thus the evolution of precipitates during service have received great attention, especially during the process of

会议

Effects of Mn and Zr addition in 6000 series aluminum alloys on the formation of stabilized substruc

Thermal stability of substructures in 6000 series aluminum alloys containing Mn and Zr elements was investigated using plane-strain compression test.In order to form thermally stabilized substructures

会议

Precipitation behaviour and mechanical properties during short-term heat treatment for tailor heat t

Precipitation hardening aluminium alloys are widely used for automotive applications.To enhance the application of aluminium profiles, improved formability is needed.Tailor Heat Treated Profiles (THTP

会议

The work hardening and strain-rate hardening behaviour of 6xxx alloys with similar yield strength

A good understanding of the work hardening and strain-rate hardening behaviour of 6xxx alloys is important for the stretch forming of such Al-Mg-Si alloys.In this study, four 6xxx alloys with differen

会议

High strength alloys for automotive applications

The aluminum industry has been developing alloys and products to address the light-weighting needs of the automotive customers.Recently, this light-weighting trend has resulted in an increased demand

会议

The effect of heating rate on the density and spatial distribution of dispersoids during homogenizat

Three 6xxx alloys with varying Mn-content have been homogenised in a furnace at 580℃ for 2 hours and 15 minutes.Three different heating rates to the homogenisation holding temperature were chosen, as

会议

The influence of quench rate on grain boundary precipitation in AA6082

Grain boundary precipitation of Mg-Si phases in 6xxx materials is known to decrease the strength of grain boundaries leading to a transition from transgranlar to intergranular failure.The extent of gr

会议

Effect of homogenization conditions on microstructures of foil stock of continuous casting and rolli

与本文相关的学术论文