TaC-SiC, one member of ultrahigh-temperature ceramics (UHTCs), is potentially useful as structural materials in aerospace engineering and hypersonic flight vehicles.In this paper, the synthesis and ch
【机 构】
：
Science and Technology on Advanced Ceramic Fibres and Composites Laboratory, National University of
【出 处】
：
2016’中国溶胶-凝胶学术研讨会暨国际论坛
论文部分内容阅读
TaC-SiC, one member of ultrahigh-temperature ceramics (UHTCs), is potentially useful as structural materials in aerospace engineering and hypersonic flight vehicles.In this paper, the synthesis and characterization of nano-tantalopolycarbosilanes (TS) and their transformation into ceramic materials are reported.The TS-5, TS-10, TS-25, and TS-55 hybrid precursors were prepared by using nanometer tantalum powders and polycarbonsilane(PCS), according to the quality of tantalum powders and PCS at 5wt%, 10wt%,25wt%, 55wt%, respectively, via ultrasonic and ball mill mixing method.The composition, structure, uniformity and pyrolysis process of the obtained precursors were investigated by infrared (IR), thermogravimetric (TGA), element analysis, SEM characterization, and so on.The results show that the nanometer tantalum powders were dispersed uniformly in PCS.The ceramic yield of the precursors increased gradually with the increase of tantalum powder proportion.The inorganic conversion was almost completed at 800 ℃ and TaC crystal appeared, metal tantalum was completely converted into TaC at 1400 ℃.As the temperature increases, the crystallization of TaC is more and more sharp which indicated the growth of TaC grain.The non-oxygen structure, high ceramic yield, and uniform composition enable the as-received hybrid precursor as promising materials to prepare high performance ultrahigh-temperature ceramics.
其他文献
Using commercial Lower melting point glass powers, Ce∶YAG phosphor powder and acrylic resin as raw materials, Ce∶YAG quartz glass phosphor films for high-power white LED have been successfully prepare
本文采用溶胶-凝胶法，以正硅酸四乙酯为前驱体，氨水为催化剂制备标准SiO2溶胶.在溶胶老化过程中使用硅烷偶联剂KH570对溶胶改性，通过浸渍提拉法在BK7玻璃上镀膜，获得高透过率且耐环境稳定性良好的SiO2减反膜.使用原子力显微镜(AFM)、扫描电子显微镜(SEM)、UV-Vis-NIR分光光度计、傅里叶变换红外光谱仪、接触角测试仪等对薄膜的性能进行表征.结果表明：当KH570与TEOS的摩尔比为
Modified organic silica sol coating was prepared on the surface of zirconium hydride (ZrH1.8) by sol-gel technology using ethyl silicate (TEOS), isopropyl alcohol (IPA) and H2O as raw materials, coupl
Nano hydroxyapatite (n-HA), polyamide 66 (PA66) and chitosan (Cs) are often use as a kind of biomaterials due to their excellent properties, especially in bone repair materials.And Erythromycin (EM) i
The ammonium molydbate(AM) based on zinc hydroxystannate(ZHS) and AM/ZHS was coated by aluminum hydroxide (ATH) with different ratios were successfully prepared via sol-gel technique.The emphasis in t
Macroporous ZnAl2O4 spinel monolith with a well-defined macropores was successfully prepared using the sol-gel process accompanied by phase separation in the presence of poly (ethylene oxide) (PEO) an
This papermainly introduced classification and the presentation of the catalytic material and zirconia properties and applications, a series of Fe-Al-Ce-ZrO2 catalytic material of hydrothermally Sol-G
LiFePO4 (LFP) and Li3V2(PO4)3 (LVP) as lithium ion battery (LIB) cathode materials have been investigated due to their advantages, such as low cost, nontoxicity and high theoretical capacity.[1,2] How
NaInO2, which has α-NaFeO2 layered-type structure, was synthesized by solid phase method with low temperature at 750 ℃ for 2h in this study.The products were characterized by X-ray diffraction (XRD),s
Mn1-xZnxFe2O4 (0≤x≤1, step:0.2) nano powders were fabricated by a template-assisted sol-gel method.The microstructure and magnetic properties of Mn1-xZnxFe2O4 were measured by XRD and VSM.The effects