The microstructure, mechanical properties, and misorientation of automobile beam steels produced by EAF-CSP process were studied using optical microscopy (OM) and electron back-scattered diffraction (EBSD). It is shown that the microstructure of strips is mainly polygonal ferrite, and the average grain size is about 5-8 μm. The electron back-scattered diffraction results show that grain boundaries in ferrite are basically high-angle grain boundaries without remarkable preferred orientation. Hot strips of automobile beam steels possess a good combination of strength and plasticity because of their fine microstructures and low quantity of impurities.
The microstructure, mechanical properties, and misorientation of automobile beam steels produced by EAF-CSP process were studied using optical microscopy (OM) and electron back-scattered diffraction (EBSD). It shows shown the microstructure of strips is mainly polygonal ferrite, and the average grain size is about 5-8 μm. The electron back-scattered diffraction results show that grain boundaries in ferrite are basically high-angle grain boundaries without remarkable preferred orientation. Hot strips of automobile beam steels possess a good combination of strength and plasticity because of their fine microstructures and low quantity of impurities.