The objective of this study was to expound a novel surgical management technique assisted by patient-specific implants(PSIs)for comminuted fractures of the zygomaticomaxillary complex(ZMC).The aim of this study was to explore the feasibility of using PSIs to accurately restore and fix comminuted fractures.A male patient with an old ZMC comminuted fracture was used to describe the workflow,technique,and method.Computer-assisted surgical simulation was used to determine the optimal plan for the reduction of bone segments prior to surgery.The PSIs were used to accurately guide the surgeon's position of the bone segments,as planned,during the operation.Oral panoramic films and cephalometric films were taken immediately at 1,3,6,and 12 months after the operation,while computed tomography images of the whole skull were taken immediately,half a year,and one year after the operation.The patient's follow-up showed that the zygomatic symmetry recovered well post-surgery and the patient was satisfied with the outcome.This new surgical method greatly improved the facial symmetry of this patient.
其他文献
采用放电等离子烧结技术(spark plasma sintering,SPS)制备铜基粉末冶金摩擦材料,研究石墨烯微片含量对铜基粉末冶金摩擦材料物理性能和摩擦磨损性能的影响。结果表明:当石墨烯微片质量分数低于4%时,材料的密度、孔隙率和抗剪切强度随石墨烯微片含量的增加而升高;当石墨烯微片质量分数超过4%后,材料的密度、孔隙率和抗剪切强度随石墨烯微片含量的增加而略微减小;石墨烯微片质量分数为4%时,铜基粉末冶金摩擦材料具有最优的摩擦性能,此时其布氏硬度为82,剪切强度为98.73 MPa。
Patient-specific instrumentation(PSI)enables a more accurate alignment of the lower limbs in a high tibial osteotomy(HTO)than in traditional surgery;however,the
采用光学显微镜、万能材料试验机和金属摆锤式冲击试验机研究了退火温度对TC4ELI钛合金大规格环材(Φ3384 mm/Φ3300 mm×1950 mm)的显微组织和力学性能的影响。显微组织分析结果表明:退火温度在850℃以下时,TC4ELI钛合金大规格环材退火后的显微组织与热加工态的显微组织基本相同;900℃退火后,TC4ELI钛合金大规格环材中部分片层状或针状α相的尺寸增大,同时出现了尺寸微小的等轴α相。力学性能测试结果表明:随着退火温度的升高,TC4ELI钛合金大规格环材的强度和伸长率有所提高;850℃
使用医用镍钛管制备拉伸试样,研究了时效温度、时效时间、循环加载次数、应变和加载速率对医用镍钛材料永久变形量的影响。结果表明:随着时效温度的升高,试样的永久变形量先增大后减小;随着时效时间的延长,试样的永久变形量增大;460℃时效30 min时,试样的永久变形量增加到3.350%;随着加载次数的增加,累积永久变形量逐渐增大,直至一定次数后趋于稳定;当应变不超过8%时,永久变形量较小(<0.100%);但随着应变增大至15%时,永久变形量增加到8.350%;随着加载速率的增加,试样的永久变形量增大。对镍
过渡金属氮化物(transition metal nitrides,TMNs)因具有硬度高、热稳定性好等特点,被作为一种硬质纳米多层薄膜在工程领域得到广泛使用。但TMNs低的韧性限制了其作为纳米多层薄膜在先进制造领域的发展。如何在保持高硬度的前提下增加薄膜的韧性,成为超硬薄膜面临的新挑战。综述了TMNs纳米多层薄膜的增韧研究进展,包括TMNs薄膜传统的增韧方法(延性相增韧、相变增韧、压应力增韧、结构优化增韧)以及通过提高价电子浓度来增强硬质陶瓷薄膜韧性的可行途径;并提出通过合理的化学成分、宏观结构(衬底约
钛合金是航空航天、军工、生物等领域重要使用材料之一,但其摩擦磨损性能较差,限制了其在摩擦工况下的应用。对比测试了TC29钛合金在不同摩擦配副和摩擦参数下的摩擦磨损性能。研究结果表明:与GCr15钢对磨时,TC29钛合金的摩擦磨损程度明显高于其与TC29钛合金对磨时的摩擦磨损程度;与GCr15钢对磨时,TC29钛合金的主要磨损机制为磨粒磨损和剥层磨损,与TC29钛合金对磨时,其主要磨损机制为黏着磨损;载荷和对磨转速的增加均会加剧TC29钛合金的摩擦磨损,但具体摩擦磨损的程度受摩擦配副情况及相应的磨损机制的影
Owing to the paucity of donor organs and their acute rejection by the immune system after transplan-tation,advanced organ failure is one of the major challenges
在气候变化的时代,人们越来越重视建筑的“绿色”资质,因为环境是影响设计、建造和运营决策的主导因素。世界各地的可持续建筑既是一道美丽的风景,又蕴藏了可持续发展的理念。像素大厦(墨尔本,澳大利亚)“像素大厦”展示了“绿色”可以是一件多色的事情。该大厦是澳大利亚第一座碳中和办公大楼,所有的电力和水都在现场产生。它的节能功能就是由它外表那些色彩鲜艳、引人注目的面板实现的。这些面板可以提供遮阳,并在需要时最大限度地利用日光。该建筑也支持废水处理,屋顶可以收集雨水,并设置了一系列垂直风力涡轮机。
当人类暂停下来,地球得以再次呼吸。你听过旧金山金门大桥下传来的啾啾鸟鸣吗?你见过十几头座头鲸“抛下”幼崽用崭新的方式“携手合作”捕鱼吗?你想象过,非洲斑嘴环企鹅行走在水泥铺就的宽阔马路穿越空无一人的街道吗?纪录片《地球改变之年》用真实的镜头记录下,当人类的行动被新冠肺炎疫情束缚,活动足迹从地球的城市、乡村、野外等角落全面撤退,地球以及居住在地球上的野生动物发生了怎样的巨大改变:汽车出行量减少,洛杉矶迎来了40年来空气质量最好的一天;沙滩上没有了度假的人类,海龟产下了数量更多的卵,幼龟成活率比以往高出了三成
为探究适合工业化生产用超疏水纳米TiO2的绿色改性工艺,以饱和脂肪酸A、硅烷B、纳米TiO2(P25)等为原料制备超疏水TiO2粉末,与环氧树脂混合后利用喷涂法制备出超疏水涂层。采用扫描电子显微镜、X射线衍射仪、傅里叶变换红外光谱仪和接触角分析仪对超疏水粉末和超疏水涂层表面的形貌和疏水性进行了表征。结果表明:超疏水TiO2粒子表面具有疏水性基团和微-纳米双重粗糙结构,粒子表面的静态水接触角为158°,滚动角为3°;当超