【摘 要】
：
在实验室条件下,研究了罩式退火温度对DC03EK搪瓷用钢组织性能的影响规律,同时对其抗鳞爆性能和搪瓷密着性能进行了检验。结果表明,730℃×5 h退火的实验钢屈服强度为148 MPa
【机 构】
：
东北大学轧制技术及连轧自动化国家重点实验室,国丰钢铁有限公司,
论文部分内容阅读
在实验室条件下,研究了罩式退火温度对DC03EK搪瓷用钢组织性能的影响规律,同时对其抗鳞爆性能和搪瓷密着性能进行了检验。结果表明,730℃×5 h退火的实验钢屈服强度为148 MPa,抗拉强度为300 MPa,断后伸长率为38%,r值为1.5,成形性能良好。1 mm厚冷轧退火板氢渗透时间为13 min,氢扩散系数为8.4×10-7cm2/s,抗鳞爆性能良好,并通过了密着性检验。
Under laboratory conditions, the influence of hood annealing temperature on the microstructure and properties of DC03EK enamel steel was studied, and its anti-scale explosion performance and enamel adhesion performance were tested. The results show that the yield strength of the experimental steel annealed at 730 ℃ × 5 h is 148 MPa, the tensile strength is 300 MPa, the elongation at break is 38%, the r value is 1.5 and the formability is good. Hydrogen permeation time of 1 mm cold-rolled annealed sheet was 13 min, hydrogen diffusion coefficient was 8.4 × 10-7cm2 / s, anti-scale explosion performance was good, and passed the test of adhesion.
其他文献
数理统计中的正交设计方法用于六角形铀氢锆堆芯燃料装载的优化计算，研制了六角形研究堆堆芯燃料管理优化计算的软件包ＨＥＸＯＲＴＨ，应用该软件包对西安脉冲堆第三循环末堆芯现有燃料装载
采用离心浇铸制备外层为碳钢Q235,内层为高铬铸铁的双金属复合管。在不同温度(950、980℃)及不同冷却方式(空冷、水冷、风冷)下对复合管进行热处理试验。结果表明,试验温度下
本文概述近几年来核数据测量、评价和计算,包括次级中子和带电粒子双微分截面、活化截面、裂变产额、中子谱和辐射俘获γ射线的实验测量,通用库全套中子数据和专用库裂变产额
在现在的时代,已经是科技信息飞速发展的时代.而且,信息技术的发展不仅慢慢的渗入了人们的生活中,并且也渗透到了对学生的教学中来.在新的二十一世纪中,信息技术的发展成为了
昨晚半决赛出现本届世界杯最大新闻:德国战车以7:1踏平巴西,虽然不是巴西球迷,我也为巴西掬了一捧泪,这也太不给东道主面子了。德国人上一次这样残酷无情还是在二战的时候哇,
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
<正>HIRFL是中国科学院近代物理研究所负责设计建造的我国第一个大型重离子物理研究装置,1988年12月建成出束.HIRFL主要由离子源、注入器、主加速器、
问题链是指在教学过程中结合课文内容将教材知识转变为一系列富有层次性、相对独立又相互关联、并且环环相扣的问题的形式,这是高中英语教学中一种非常有效的教学模式.笔者在
随着素质教育的发展,小学日益重视体育教学。体育教学是小学教育的重要组成部分,对于促进学生的全面发展,提高学生的体质,确保学生的身心健康具有至关重要的作用和意义。然而
本文报道一个时间投影室（ＴｉｍｅＰｒｏｊｅｃｔｉｏｎＣｈａｍｂｅｒ，ＴＰＣ）模型（１００ｍｍ×１００ｍｍ×５８ｍｍ）的设计和利用矩阵电容法计算ＴＰＣ内电场强度的结果。在ＴＰＣ漂移区配置等压环后，在Ｘ±３０ｍｍ和Ｘ±４０ｍｍ区域内，漂移区电场均匀度分别为０．９％和３％。
This paper reports t