论文部分内容阅读
According to traditional phenomenological fatigue methodology and mod continuum damage mechanics theory, dual fatigue cumulative damage rules to predict fatigue damage formation and propagation lives of the notched composite laminates are presented.A 3-dimensional damage constitutive equation of anisotropic composites is also established.Damage strain energy release rate is interpreted as a driving force of the fatigue delamination damage propagation.A new damage evolution equation and a damage propagation (a-(m-N( surface (stress amplitude-mean stress-life surface) are derived.Hence, using the method above, the fatigue life of composite components can be predicted.Finally, theoretically predicted results are compared with experimental data.It is found that the deviation of theoretic prediction from experimental results is about 22%.