Supermacroporous composite cryogels embedded with SiO2 nanoparticles were prepared by radical cryogenic copolymerization of the reactive monomer mixture of acrylamide(AAm) and N,N-methylene-bis-acrylamide(MBAAm) containing SiO2 nanoparticles(mass ratios of nanoparticles to the monomer AAm from 0.01 to 0.08) under the freezing-temperature variation condition in glass columns.The properties of these composite cryogels were measured.The height equivalent to theoretical plate(HETP) of the cryogel beds at different liquid flow rates was determined by residence time distribution(RTD) using tracer pulse-response method.The composite cryogel matrix embedded with the mass fraction of SiO2 nanoparticles of 0.02 presented the best properties and was employed in the following graft polymerization.Chromatographic process of lysozyme in the composite cryogel grafted with 2-acrylamido-2-methyl-1-propanesulfonic acid(AMPSA) was carried out to evaluate the protein breakthrough and elution characteristics.The chromatography can be carried out at relatively high superficial velocity,i.e.,15 cm·min-1,indicating the satisfactory mechanical strength due to the embedded nanoparticles.
Supermacroporous composite cryogels embedded with SiO2 nanoparticles were prepared by radical cryogenic copolymerization of the reactive monomer mixture of acrylamide (AAm) and N, N-methylene-bis-acrylamide (MBAAm) containing SiO2 nanoparticles (mass ratios of nanoparticles to the monomer AAm from 0.01 to 0.08) under the freezing-temperature variation condition in glass columns. The properties of these composite cryogels were measured. The height equivalent to theoretical plate (HETP) of the cryogel beds at different liquid flow rates was determined by residence time distribution (RTD) using tracer pulse-response method. The composite cryogel matrix embedded with the mass fraction of SiO2 nanoparticles of 0.02 presented the best properties and was employed in the following graft polymerization. Chromatographic process of lysozyme in the composite cryogel grafted with 2-acrylamido-2- methyl-1-propanesulfonic acid (AMPSA) was carried out to evaluate the protein breakthrough and elution characteristi The chromatography can be carried out at relatively high superficial velocity, ie, 15 cm · min-1, indicating the satisfactory mechanical strength due to the embedded nanoparticles.