Two kinds of cold rolling experiments, single cold rolling and double cold rolling, were carried out on one titanium stabilized interstitial free (IF) steel that has been warm rolled at ferrite temperature. The main aim was to investigate the evolution of rolling and annealing textures from the well known behavior observed under single cold rolling condition to the less understood double cold rolling by using orientation distribution function (ODF). In the twice cold rolled samples, the annealing texture comprises only single {111}(110-112) r-fibre texture when it subjected to moderate reduction in the first round of rolling. Accordingly both the once cold rolled sample and the twice cold rolled sample with heavy reduction in the first round of rolling have much complex texture components. They are related to the formation of initial {111} subgrain and the priority growth of stable {111} nucleus.
Two kinds of cold rolling experiments, single cold rolling and double cold rolling, were carried out on one titanium stabilized interstitial free (IF) steel that has been warm rolled at ferrite temperature. The main aim was to investigate the evolution of rolling and annealing textures from the well known behavior observed under single cold rolling conditions to the less understood double cold rolling by using orientation distribution function (ODF). fiber both when once cold rolled sample and the twice cold rolled sample with heavy reduction in the first round of rolling have much complex texture components. They are related to the formation of initial {111} subgrain and the priority growth of stable {111} nucleus.