In order to study the influence of the physical state of solder on the interfacial reaction of dip-soldered Sn-3.0Ag-0.5Cu/Cu system,two kinds of experiments were designed,including:(1) solid-state aging between the solder and Cu substrate;(2) liquid-stat
【机 构】
：
Key Lab for Robot and Welding Automation of Jiangxi Province, Mechanical and Electrical Engineering
论文部分内容阅读
In order to study the influence of the physical state of solder on the interfacial reaction of dip-soldered Sn-3.0Ag-0.5Cu/Cu system,two kinds of experiments were designed,including:(1) solid-state aging between the solder and Cu substrate;(2) liquid-state aging between the metastable supercooled liquid-state solder and Cu substrate.The aging times were 30,60,120 and 180 rnin,respectively,and the aging temperature was 8 ℃ lower than the melting point of the Sn-3.0Ag-0.5Cu (SAC305) alloy (217 ℃).The experimental data revealed that the physical state of the solder obviously affected the formation of the intermetallic compound (IMC),and resulted in the difference in the diffusion of atoms on the interface between the SAC305 solder and Cu substrate.The IMC interface after aging for 30 min presents unique characteristics compared with that of the sample after dip soldering.The IMC interface of solid-state aged SAC305/Cu couple is relatively planar,while the IMC interface under metastable supercooled liquid-state aging conditions presents scallop-like shape.
其他文献
Ni-based self-lubricating composites containing a fixed amount of hexagonal boron nitride (h-BN) (5 wt％) and different amounts of graphene (0-1.5 wt％) were prepared by ultrasonic dispersion,high-energy ball milling,and spark plasma sintering.The effects o
The corrosion behavior of high-strength steel used for flexible riser exposed to CO2-saturated saline solution and CO2-saturated vapor environments was studied through immersion experiment and electrochemical corrosion experiment.The corrosion behavior an
The effect of hot isostatic pressing (HIP) treatment on the fatigue notch sensitivity of Ti-6Al-4V alloy fabricated by electron beam melting (EBM) was investigated.The results indicate that the fatigue notch sensitivity of the as-fabricated samples is muc
Porous titanium scaffold with suitable porous architecture exhibits enormous potentials for bone defect repairs.However,insufficient osteointegration and osteoinduction still remain to open as one of the major problems to achieve satisfactory therapeutic
The study conveys an idea to enhance the osseointegration of titanium implant (Ti) through modulating macrophages M2 polarization.The ～ 100 nm spherical mesoporous silica nanoparticles (MSN) that compromised of ～ 4-nm-diameter nanotunnels were synthesized
The residual stress evolution in a safe-end/nozzle dissimilar metal welded joint of CAP1400 nuclear power plants was investigated in the manufacturing process by finite element simulation.A finite element model,including cladding,buttering,post-weld heat
The effects of Ni content and ball milling time on the hydrogen storage thermodynamics and kinetics performances of asmilled La5Mg95-xNix(x =5,10,15) ternary alloys have been investigated.The evolution of microstructure and phase of experimental alloys in
A large amount of directional and willow-like β\'phase was precipitated in Mg-10Gd-3Y-0.4Zr (GW103K) alloy after solution treatment and subsequently aged treatment (T6).In order to explore the effect of the precipitates on the corrosion behavior of the
Nanocrystalline and amorphous NdMg12-type NdMg11Ni +x wt％ Ni (x=100,200) alloys were successfully prepared through ball milling (BM).The microstructures and electrochemical properties were systematically studied to get a more comprehensive understanding o
The effect of phosphorus on the precipitations of γ“,γ\'and δ phases and associated tensile properties in IN718C alloy are investigated in this study.It is revealed that P atoms are dissolved in the grain interior to a relatively high degree and hence i