【摘 要】
：
采用流变铸造法制备了ＳｉＣｐ／Ｚｎ基复合材料，对该材料进行了弯曲强度、冲击韧性、压缩强度、硬度及耐磨性等性能试验，结果表明：ＳｉＣｐ的加入，使锌合金的压缩强度、室温和高温硬度以及耐磨性明显提
论文部分内容阅读
采用流变铸造法制备了ＳｉＣｐ／Ｚｎ基复合材料，对该材料进行了弯曲强度、冲击韧性、压缩强度、硬度及耐磨性等性能试验，结果表明：ＳｉＣｐ的加入，使锌合金的压缩强度、室温和高温硬度以及耐磨性明显提高，其弯曲强度略有降低，而其冲击韧性下降３～５倍。最后还讨论了颗粒含量、颗粒直径以及基体特性对该复合材料性能的影响。
SiCp / Zn matrix composites were prepared by rheological casting. The flexural strength, impact toughness, compressive strength, hardness and wear resistance of the composites were tested. The results show that the compressive strength , Room temperature and high temperature hardness and wear resistance improved significantly, the bending strength decreased slightly, while the impact toughness decreased 3 to 5 times. Finally, the effects of particle content, particle diameter and matrix properties on the properties of the composites were also discussed.
其他文献
《给流浪猫一份工作》…………………………………汤小小栖身图书馆的流浪猫丽塔成了学生们的开心果,让寂寞的阅读变得趣味横生。然而校长却认为丽塔不仅影响学校的形象,有可
在研究了以稻壳为原料生长的β-SiC汇颗粒富碳的机理和形态的基础上，采用高温除碳、细磨、酸浸脱氧工艺处理，成功地获得了纯度98％以上的β-SiC汇微粉，产品经过XPS、XRD及能谱仪等
本文分析了以Lanxide技术合成AlN的生长过程，发现AlN晶体生长具有明显的方向性，XRD分析表明：AlN晶体的生长方向为[0001]晶向.反应过程中AlN由基体表面向气氛中不断深入生长，形成
探讨了WO3薄膜与1MLiClO4－PC溶液之间的界面电位差的变化规律及测量方法。制备了三种具有不同电致变色性能的WO3薄膜，并对它们进行了界面电位差随Li+注入量大小变化的测量。通
关于环氧树脂／炭纤维复合材料工艺参数的研究Ｎａｒｃｉｓｏ－ＲｏｍｅｒｏＦＪ．、ＥｄｉｅＤ．、Ｒｏｄｒｉｇｕｅｚ－ＲｅｉｎｏｓｏＦ．１引言纤维增强复合材料由夹在基体内的高强度、高模量纤维构成。虽然纤维和基体都保持着各自的性质和化学特性，但由它们构成的复
对用低压浸渗法制备石墨（碳）长纤维镁基复合材料进行了研究。结果表明，制备工艺条件对复合状况、界面反应及复合材料性能均有明显影响。通过纤维表面ＳｉＯ２涂层处理和优化浸渗工艺，可成
二进小波变换在复合材料损伤检测中的应用吴耀军陶宝祺史习智（上海交通大学振动冲击噪声国家重点实验室上海２０００３０）（南京航空航天大学智能材料和结构研究所南京２１００１６）０引言近几年来
一条远道而来的河 从一片草原流过 远远地看过去 草原像是河流的翅膀 再远远地看过去 河流像是草原的脉络 叮咚的河水 向草原唠叨着一路的疲劳 摇曳的水草 抚摸着河流柔软的脸庞 一条鱼儿跃出水面 咬住一株芦苇盛开的花 几只青蛙从草地跳进河里 让河流的心也绿了 河流很大方 给整片草原提供水分 从草叶上滴落的露珠 是草原送给河流最好的礼物 草原有光荣的使命 养育撒欢的
研究了硬对软（ＣＳ）、软对硬（ＣＨ）和软硬中（ＳＨＭ）三种典型的力学性能非对称焊接接头疲劳裂纹扩展规律．结果表明：力学性能非对称性对焊接接头的疲劳裂纹扩展规律有很大影响．起始裂纹在软区的硬对软
本刊讯学习贯彻卫留成书记关于立法工作的五点指示和省委《关于转发中共海南省人大常委会党组关于〈海南国际旅游岛建设发展专项立法计划〉的请示》的通知精神,部署海南国际