对梅钢热轧板厂所生产的带钢边部损伤缺陷及产生原因进行了描述与分析,提出了在轧制过程中热轧带钢从卷取侧导板的磨损沟槽中逃逸是产生边部损伤缺陷的根本原因,并依据分析结果提出并实施了一系列预防措施,取得了良好效果。 Described and analyzed the defects of the strip edges produced by the hot-rolled sheet mill in Meishan Iron and Steel Co., Ltd. and the reasons for their occurrence, and proposed that the escape of the hot-rolled strip from the wear grooves of the winding-side guide during the rolling process is the result of Department of the root causes of injury defects, and based on the analysis results put forward and implemented a series of preventive measures, and achieved good results.