38X2M10A钢由于氮化后具有很高的表面硬度,因此被最广泛地用于制造氮化零件。但38X2钢也有一些不足之处,其中主要缺点是其氮化层具有脆性。 38X2钾氮化后表面具有高硬度
38X2M10A steel is the most widely used nitride part for its high surface hardness after nitriding. But 38X2 steel also has some shortcomings, the main disadvantage is that its nitride layer has brittleness. 38X2 potassium nitride surface has a high hardness