Large quantity of fine Ti(C,N) particles, 15-30 nm in size, were observed in low carbon hot strips added to a small amount of Ti and produced by CSP process. The results showed that the precipitation of Ti(C,N) mostly took place during soaking and hot rolling, which is significantly different from that in the conventional production. These fine Ti carbonitride particles could be very effective on the austenite grain refinement by hindering grain growth of recrystallized austenite. Their precipitation behavior was discussed and compared with that of the steels produced in the conventional production.
Large quantities of fine Ti (C, N) particles, 15-30 nm in size, were observed in low carbon hot strips added to a small amount of Ti and produced by CSP process. The results showed that the precipitation of Ti (C, N) mostly took place during soaking and hot rolling, which is significantly different from that in the conventional production. These fine Ti carbonitride particles could be very effective on the austenite grain refinement by hindering grain growth of recrystallized austenite. Their precipitation behavior was discussed and compared with that of the steels produced in the conventional production.