【摘 要】
:
The acid treatment process,testing methods,microstrcture of sepiolite mineral materials and their adsorbing properties to dodecanol were studied respectively. T
【机 构】
:
Institute of Power Source and Ecomaterials Science
论文部分内容阅读
The acid treatment process,testing methods,microstrcture of sepiolite mineral materials and their adsorbing properties to dodecanol were studied respectively. The results show that by acid treatment to raw sepiolite thinner fibre clusters and single fibres turn up,the pore volume and the number of micropore and mesopore in sepiolite all increase,and adsorbing properties of modified sepiolite to dodecanol are improved significantly. In the combined materials of dodecanol and sepiolite prepared under the best condition,the proportion of dodecanol is 67.96%,and then it is much higher than the result calculated from traditional BET method.
其他文献
Compositional graded BaxSr1-xTiO3 (x=0.6,0.7,0.8,0.9,1.0) (BST) thin films (less than 400 nm) were fabricated on Si and Pt/Ti/SiO2/Si substrates by sol-gel tech
Low temperature sintering NiCuZn ferrite was employed at most cases due to its co-firability with Ag (below 960 ℃). The NiCuZn ferrite sintered body with high-
The carbon nanotube (CNT) growth of iron oxide-deposited trench-patterns and the locally-ordered CNT arrays on silicon substrate were achieved by simple thermal
Electrochemical methods were applied to investigate the corrosion behaviour of LY12CZ under applied stress in 3% sodium chloride aqueous solution. The experimen
A new metastable beta titanium alloy of Ti-Al-Mo-V-Cr-Fe-Zr-Sn system was designed and named Ti-B20. In order to investigate the aging properties and microstruc
Mg-6Al-4RE-0.4Mn (mass fraction, %, RE=Ce rich mischmetal) alloy was prepared by steel mould casting technique. Solid solution and artificial aging (T6) were ca
Y-shaped structure was synthesized by ethanol catalytic combustion(ECC) technique on the copper plate substrate,without directly seeding catalyst into the flame
Mg-(5-22)(mass fraction, %)Li alloys with Zn addition were produced and studied. The density of studied alloys is 1.19- 1.62 g/cm3. It is found that the alloy h
InAs quantum dots (QDs) grown on InxGa1-xAs/InP matrix by low pressure metal organic vapor phase epitaxy (LP-MOVPE) in nitrogen ambient were studied. Formation
Single crystals of Ca3NbGa3Si2O14 (CNGS) with ordered Ca3Ga2Ge4O14 (CGG) structure were successfully grown from stoichiometric melts by conventional Czochralski