【摘 要】
：
Low temperature sintering NiCuZn ferrite was employed at most cases due to its co-firability with Ag (below 960 ℃). The NiCuZn ferrite sintered body with high-
【机 构】
：
Research Center of High Technology,Advanced Science Research Center
论文部分内容阅读
Low temperature sintering NiCuZn ferrite was employed at most cases due to its co-firability with Ag (below 960 ℃). The NiCuZn ferrite sintered body with high-strength and high-frequency magnetic properties was fabricated. Firstly,NiCuZn ferrite powder was synthesized under CO2 atmosphere at 500 ℃ from the mixed doxalate synthesized by liquid phase precipitation method. Then a small amount of boric acid (H3BO3) was added to the powder,and the NiCuZn ferrite powder compact was prepared with Newton press and CIP methods. Finally,NiCuZn ferrite sintered body was fabricated by sintering at 900 ℃ under CO2 atmosphere. The minimum sintering temperature (800 ℃) was determined by the study of high temperature shrinkage. By this method,NiCuZn ferrite sintered body with 0.5% (mass fraction) boric acid was obtained,which has the bending strength of 340 MPa. The effect of various Mn addition on electromagnetic properties were studied.
其他文献
Transparent polycrystalline yttria is a promising optical ceramics with excellent physical and chemical properties. A commercial yttria powder with a mean parti
The formation ability and thermal stability of phosphate laser protection glass doped with high Sm2O3 content were discussed. The characteristic temperatures (T
316L stainless steel samples,as a widespread used material,were irradiated with HIPIB at the beam parameters of ion energy 300 keV,current density 100,200 and 3
The existence of yttrium in Ti-23Al-25Nb alloy and its influence on the microstructure after heat treatment of Ti-23Al-25Nb alloy were investigated using therma
Dipolar relaxation and dielectric/piezoelectric resonance in a (001)-cut Pb(Zn1/3Nb2/3)0.9Ti0.1O3 (PZNT10%) single crystal before and after electric (E)-field p
Three different coatings, Cr, SiO2/Cr and HfO2/SiO2 were deposited by electron beam physical vapor deposition (EB-PVD). Relevant composition and mechanical prop
A novel Al-based composite material (Al63Cu25Fe12)p/A356 was prepared by spray co-deposition. It is revealed that the reinforcement of Al63Cu25Fe12 quasicrystal
The corrosion behavior of a CuCrNiAl alloy in HCl solutions was studied by means of metallograph, XRD, SEM/EDX and TEM methods. The results show that in low con
Current—voltage (I—V) and capacitance-voltage (C—V) characteristics of Au/p-CZT contacts with different surface treatments on cadmium zinc telluride (CZT) wa
Compositional graded BaxSr1-xTiO3 (x=0.6,0.7,0.8,0.9,1.0) (BST) thin films (less than 400 nm) were fabricated on Si and Pt/Ti/SiO2/Si substrates by sol-gel tech