Poly(4-vinylpyridine)(P4-VP) nanofiber and fluoresent poly(4-vinylpyridine)/porphyrin(P4-VP/TPPA) nanofiber were respectively prepared by electrospinning. The effect of the concentration of P4-VP/dimethylformamide (DMF) electrospinning solutions on the morphology of P4-VP nanofiber was investigated and it was found that the average diameter of the nanofiber of P4-VP/DMF increased with the increase of the concentration of the spinning solution. After the addition of TPPA to the P4-VP/DMF spinning solution, the diameter of P4-VP/TPPA nanofiber became even due to the increase of the conductivity of the P4-VP/DMF-TPPA solution. The photoluminescent(PL) spectral analysis indicates that the emission peak position of P4-VP/TPPA nanofiber is almost the same as that of pure TPPA at about 650 nm without peak shift, and when it was stored for 20 days, the emission peak of P4-VP/TPPA nanofiber is also at 650 nm, indicating that the fluorescent property of P4-VP/TPPA nanofiber is stable. Fourier-transform infrared(FTIR) spectrum confirms the chemical composition of the resulting P4-VP/TPPA composite nanofiber.
Poly (4-vinylpyridine) (P4-VP) nanofiber and fluoresent poly (4-vinylpyridine) / porphyrin (P4- VP / TPPA) nanofiber were respectively prepared by electrospinning. The effect of the concentration of P4-VP / dimethylformamide electrospinning solutions on the morphology of P4-VP nanofiber was investigated and it was found that the average diameter of the nanofiber of P4-VP / DMF increased with the increase of the concentration of the spinning solution. After the addition of TPPA to the P4- VP / DMF spinning solution, the diameter of P4-VP / TPPA nanofiber became even due to the increase of the conductivity of the P4- VP / DMF-TPPA solution. The photoluminescent (PL) spectral analysis indicates that the emission peak position of P4 -VP / TPPA nanofiber is almost the same as that of pure TPPA at about 650 nm without peak shift, and when was was stored for 20 days, the emission peak of P4-VP / TPPA nanofiber is also at 650 nm, indicating that the fluorescent property of P4-VP / TPPA nanofiber is stable. Fourier-tr ansform infrared (FTIR) spectrum confirms the chemical composition of the resulting P4-VP / TPPA composite nanofiber.