论文部分内容阅读
Transmission electron microscopy (TEM) was applied to investigate the evolution of dislocation configuration and straininduced precipitation behavior during relaxation process after deformation in Fe-Ni-Nb-Ti-C-B alloy. Experimental results indicatethai t