【摘 要】
：
Due to the increasing criticality of rare earth elements (REEs),it has become essential to recover REEs from alternative resources.In this study,systematic REEs leaching tests were performed on the calci-nation product of a coal coarse refuse using hydroc
【机 构】
：
Department of Mining and Minerals Engineering,Virginia Polytechnic Institute and State University,Bl
论文部分内容阅读
Due to the increasing criticality of rare earth elements (REEs),it has become essential to recover REEs from alternative resources.In this study,systematic REEs leaching tests were performed on the calci-nation product of a coal coarse refuse using hydrochloric acid and different types of organic acid as lixiviants.Experimental results show that the recovery of REEs,especially heavy REEs (HREEs) and scandium (Sc),is improved by using selected organic acids.Citric acid and DL-malic acid afford the best leaching performances;whereas,malonic acid,oxalic acid,and DL-tartaric acid are inferior to hydro-chloric acid.Results of zeta potential measurements and solution chemical equilibrium calculations show that malonic acid is more likely adsorbed on the surface of the calcined material compared with citric acid and DL-malic acid.The adsorption may reduce the effective concentration of malonic species in solution and/or increase the amount of REEs adsorbed on the surface,thereby impairing the leaching recovery.Compared with light REEs (LREEs),a stronger adsorption of the HREEs on the surface is observed from electro-kinetic test results.This finding explains why organic acids impose a more positive impact on the leaching recovery of HREEs.By complexing with the HREEs,organic acids can keep the metal ions in solution and improve the leaching recovery.The adsorption of Sc3+ on the surface is the lowest compared with other REEs.Therefore,rather than complexing,the organic anionic species likely play a function of solubilizing Sc from the solid,which is similar to that of hydrogen ions.
其他文献
CaWO4∶xEu3+,yTm3+ crystals were obtained by facile synthesis at low temperature by the microwave-assisted hydrothermal method (MAH).The phase formation,morphology,luminescent properties and energy transfer were investigated.The X-ray diffraction (XRD) res
While the versatile composition of layered double hydroxides (LDHs) allows the introduction of almost any polyvalent cation in their structure,the exchangeable negatively charged ions intercalated between the plates increase their vast range of functional
In this paper,Dy3+ incorporated BaSi2O5 phosphors were synthesized by gel combustion method and char-acterized by X-ray diffraction (XRD).The effects of various heating rates on thermoluminescence (TL) kinetics and glow peak temperatures of Dy3+ incorpora
Mn2+ doped LuAG phosphors with different contents of Si4+ ions were synthesized via the solid-state reaction method and the effects of Si4+ doping on the crystal structure and luminescence properties of phosphors were studied.XRD patterns of all phosphors
This study explored the superior citrate method (CM) to synthesize Mn-Ce bi-oxides on 3D monolithic Ni-foam (NF) catalysts for the selective catalytic reduction of NO by NH3 (NH3-SCR).The 17 wt％ Mn(7)Ce(3)Ox/NF (CM-17) catalyst shows the NOx conversion of
Nanostructured HoFeO3 powders were obtained by solution combustion method at various glycine-nitrate ratios (G/N =0.2,0.4… 1.4).According to X-ray powder diffractometry data,the presence of two modifications of HoFeO3 in the synthesized samples was establ
The samples with full density were prepared by hot pressing the the melt-spun powders mixed with DyF3 powders of different mass fractions followed by hot-deformation process.The magnetic properties and temperature dependence of coercivity were obtained by
Rare earth passivation was conducted on Zn coated NdFeB magnets by chemical reaction to enhance the corrosion resistance performance.Morphologies,microstructures and compositions of different passiv-ated coatings were studied by X-ray diffraction,field em
Doping and coating are frequently employed for the improvement of the properties of Ni-rich NCM materials.In this work,we prepared stable LiNi0.8Co0.1Mn0.1O2 (NCM811) materials modified with Y2O3 via a wet chemical method.In order to investigate the actio
Herein,sodium dodecylbenzene sulfonate (SDBS) was used as a template to control the synthesis of Ca0.5Pr0.5FeO3.Its microstructure,composition,and morphology were detected via X-ray diffraction(XRD),Fourier transform infrared spectroscopy (FT-IR),and scan