In order to investigate the influences of the stoichiometric ratio of B/A (A: gross A-site elements, B: gross B-site elements) and the substitution of Co for Ni on the structures and electrochemical performances of the AB3.5-4.1-type electrode alloys, the La-Mg-Ni-Co system La0.75Mg0.25Ni3.5Mx (M=Ni, Co; x= 0, 0.2, 0.4, 0.6) alloys were prepared by induction melting in a helium atmosphere. The structures and electrochemical performances of the alloys were systemically measured. The results show that the structures and electrochemical performances of the alloys are closely relevant to the B/A ratio. All the alloys exhibit a multiphase structure, including two major phases, (La, Mg)2Ni7 and LaNi5, and a residual phase LaNi2, and with rising ratio B/A, the (La,Mg)2Ni7 phase decreases and the LaNi5 phase increases significantly. When ratio B/A=3.7, the alloys obtain the maximum discharge capacities. The high rate discharge(HRD) capability of the alloy (M=Ni) monotonously rises with growing B/A ratio, but that of the alloy (M=Co) first mounts up then declines. The cycle stability of the alloy (M=Co) monotonously increases with rising B/A ratio, but it first decreases slightly then increases for the alloy (M=Ni). The discharge potential of the alloy (M=Ni) declines with increasing B/A ratio (x>0.2), but for the alloy (M=Co), the result is contrary. The substitution of Co for Ni significantly ameliorates the electrochemical performances. For a fixed ratio B/A=3.7, the Co substitution enhances the discharge capacity from 365.7 to 401.8 mA·h/g, the capacity retention ratio (S100) after 100 charging-discharging cycles from 50.32% to 53.26% and the HRD from 88.65% to 90.69%. In order to investigate the influences of the stoichiometric ratio of B / A (A: gross A-site elements, B: gross B-site elements) and the substitution of Co for Ni on the structures and electrochemical performances of the AB3.5- 4.1-type electrode alloys, the La-Mg-Ni-Co system La0.75Mg0.25Ni3.5Mx (M = Ni, Co; x = 0, 0.2, 0.4, 0.6) alloys were prepared by induction melting in a helium atmosphere. The structures and electrochemical performances of the alloys were systemically measured. The results show that the structures and electrochemical performances of the alloys are closely relevant to the B / A ratio. All the alloys exhibit a multiphase structure, including two major phases, (La, (Ratio of Mg, Mg) 2Ni7 and LaNi5, and a residual phase LaNi2, and with rising ratio B / A, the (La, Mg) 2Ni7 phase decreases and the LaNi5 phase are significantly increased. When ratio B / A = 3.7, capacities. The high rate discharge (HRD) capability of the alloy (M = Ni) monotonously rises with growing B / A ratio, but that of the alloy (M = Co) first mounts up then declines. The cycle stability of the alloy (M = Co) monotonously increases with rising B / A ratio, but it first reduces slightly then increases for the The discharge potential of the alloy (M = Ni) declines with increasing B / A ratio (x> 0.2), but for the alloy (M = Co) For Ni significantly ameliorates the electrochemical performances. For a fixed ratio B / A = 3.7, the Co substitution enhances the discharge capacity from 365.7 to 401.8 mA · h / g, the capacity retention ratio (S100) after 100 charging-discharging cycles from 50.32 % to 53.26% and the HRD from 88.65% to 90.69%.