加气混凝土和加气硅酸盐制品的蒸压循环时间一般由两个因素决定:一是制品在蒸压釜中升温到蒸压处理最高温度的时间;二是残留游离氧化钙化合生成水化硅酸钙所需要的时间。只有采用最佳蒸压制度才能确保石灰尽快充分化合生成水化硅酸钙。全苏建筑材料科学研究所等单位近年来研究成功一种蒸压加气混凝土制品的快速升温工艺,这一工艺经过在一些加气混凝土工厂的试点应用,取得了很好的效果。 The autoclaving cycle time of aerated concrete and air-entrained silicate products is generally determined by two factors: first, the temperature at which the product is heated to the maximum autoclave temperature in an autoclave; and secondly, residual free calcium oxide combines to generate hydration. The time required for calcium silicate. Only the best autoclave system is used to ensure that lime is fully combined with calcium silicate as quickly as possible. In recent years, the Institute of Building Materials Science and Technology of Quanzhou University has successfully researched a rapid temperature increase process for autoclaved aerated concrete products. This process has achieved good results after pilot application in some aerated concrete factories.