【摘 要】
：
以聚氯乙烯(PVC)和月桂酸钠为原料,通过化学接枝法获得可侧链结晶的梳形PVC。利用FT-IR、1 H-NMR、GPC和DSC对接枝PVC的结构和结晶性能进行表征。结果表明:梳形侧链已成功接
论文部分内容阅读
以聚氯乙烯(PVC)和月桂酸钠为原料,通过化学接枝法获得可侧链结晶的梳形PVC。利用FT-IR、1 H-NMR、GPC和DSC对接枝PVC的结构和结晶性能进行表征。结果表明:梳形侧链已成功接枝到PVC上,并形成侧链结晶。随着接枝率的提高,侧链结晶熔融焓增大。在反应温度70℃、反应时间9h、接枝物摩尔用量为50%时,接枝率较高,达6.72%,侧链结晶熔融焓约为13.4J/g。
Polyvinyl chloride (PVC) and sodium laurate as raw materials, by chemical grafting method to obtain side chain crystal comb PVC. The structure and crystallinity of grafted PVC were characterized by FT-IR, 1 H-NMR, GPC and DSC. The results showed that the comb-type side chain has been successfully grafted onto PVC and formed side-chain crystals. As the grafting rate increases, the enthalpy of side-chain crystallization increases. When the reaction temperature was 70 ℃, the reaction time was 9h and the molar amount of the graft was 50%, the grafting rate was high at 6.72%, and the enthalpy of side chain crystallization was about 13.4J / g.
其他文献
为保证地甲病区人民吃上合格的碘盐,推动食盐加碘防治地甲病工作的开展,轻工业部、卫生部、商业部和中共中央地方病防治领导小组办公室,于去年十一月二十日至二十三日在河南
为研究肿瘤抑制基因Ｐ５３与卵巢癌的关系，用多聚酶链反应－单链构象多态（ＰＣＲ－ＳＳＣＰ）银染技术检测了３０例上皮性卵巢癌中Ｐ５３基因第５～８外显子的点突变。结果；ＳＳＣＰ阳性１２例，阳性率为４０％，第５、６、７外显子分别为１、２、９例。Ｐ５３基因点
为了探讨HPV和HSV—2在人子宫颈癌发病中的作用,我们利用~(32)P标记的HPV—16和HSV—2 DNA探针和打点杂交技术对西安地区29例人子宫颈浸润癌进行了研究。结果发现,23/29例(7
近年来随着城乡的工业改革,化学工业的迅速发展,乡镇企业的出现,在生产环境中,生产和使用化学物质日益增多,但安全及劳动保护措施重视不够,以致造成某些化学物质对人体皮肤
设计了一种全硅胶植入式腹腔内化疗导管系统。该装置以医用硅橡胶为原料，由储药盒和导管组成。药盒体积４．８ｍｌ，有效穿刺面积３．１４ｃｍ２。导管内外径为５ｍｍ和７ｍｍ。本装置用于治疗１６例卵巢恶性肿瘤和１例原发
1980年以来,我们应用654—2注射液治疗输液反应128例,效果良好,现报道如下.一、临床资料本文128例中男性76例,女性52例,年龄最小者3岁半,最大者74岁,22岁至40岁者最多.本组
宫腔镜在幼女阴道疾病的应用章桂红，姜琪，高琴我院应用宫腔镜检查幼女１８例，提高了诊断准确性，方法简便而安全，今报道供参考。临床资料本院自１９８４年１月至１９９３年１２月，诊治幼女阴道疾病１８例，年龄平均３．６岁
经过思想酝酿和组织准备,上海地区文献资源共享共建协作签字仪式于1994年3月14日在上海图书馆隆重举行。上海图书馆朱庆祚馆长主持签字仪式,吴建中副馆长汇报了上海地区文献
卵巢囊性畸胎瘤并同侧浆液性囊腺瘤１例江苏锡州市第一人民医院韩欣宁，李士华患者１８岁，未婚。固下腹痛１８小时，妇检发现盆腔包块于１９９４年９月７日入院。查体：痛苦面容，心肺（－），腹软，下腹压痛及反跳痛（＋），耻
输卵管恶性中胚叶混合瘤１例胡东升（解放军５３４医院病理科河南洛阳４７１００３）患者女性，５９岁。阴道不规则流棕色液体伴右下腹隐痛不适３月余。绝经１０年。查体：右下腹可扪及一蜡肠样肿物，约３ｃｍ×８ｃｍ，轻压痛。手术