A new hydrometallurgical process for a carbonaceous refractory gold concentrate at ambient temperature and pressure was presented, including grinding-leaching,
【机 构】
：
Institute of Metal Research
论文部分内容阅读
A new hydrometallurgical process for a carbonaceous refractory gold concentrate at ambient temperature and pressure was presented, including grinding-leaching, intensified alkaline leaching(IAL), thiosulfate leaching and cementation by zinc powder. The experimental results show that the grinding-leaching and intensified alkaline leaching process result in the selective oxidation of arsenopyrite and pyrite. The oxidation ratio of As is 96.6%, and 46.7 % for S. The total consumption of NaOH in alkaline leaching is only 28 % of that theoretically calculated under the conditions of full oxidization for the same amount of arsenopyrite and pyrite transforming into arsenates and sulfates, and 83. 6 % of gold is synchro-dissoluted by thiosulfate self-generated during pretreatment. Since the carbonaceous matter in concentrate possesses a strong capability of preg robbing, the cyanidation process is not suitable for the extraction of gold after pretreatment. However, the gold leaching rate by thiosulfate leaching for 24 h is increased to 91.7% from 0 - 3.2% by ultra-fine grinding without the pretreatment. The recovery of gold by zinc cementation gets to 99.6 %. Due to the thiosulfate self-generated during alkaline leaching, the reagent addition in thiosulfate leaching afterwards is lower than the normal one.
其他文献
Although biometallic materials have been used as bone implant materials for a long time, they are still detected as foreign bodies by human immune system. Calci
The reverse microemulsion composition consisting of 37. 0% cyclohexane, 26.0% surfactant (TX-10and AEO9), 13.0% n-pentanol and 24.0% aqueous phase was investiga
External cooling technology is one of the key technologies to realize fast-casting-rolling process of aluminum, i.e. using compulsive cooling on the external su
The films of octadecene, dodecene, and undecenoic acid were prepared on H-terminated Si surface in the presence of ultraviolet irradiation. The resulted films w
Thermoelectric materials, Mg2Si1-xGex (x=0, 0.2, 0.4, 0.6, 0.8, 1), have been prepared by bulk mechanical alloying (BMA) and hot pressing (HP). The electrical c
This paper presents results of combustion synthesis (Self-Propagating High Temperature Synt hesis, SHS) of Si3N4under nitrogen with argon, hydrogen or ammonia.
The kinetics of La-Co alloy film in acetamide-urea-NaBr molten salt electrolyte at 353 K was investigated. It is shown that the reduction of Co( Ⅱ ) to Co is i
A new method using lead coated glass fiber to produce continuous wire for battery grid of electric vehicles (EVs)and hybrid electric vehicles (HEVs) was introdu
An information model is defined to support sharing scientific information on Web for archaeological pottery. Apart from non-shape information, such as age, mate
Support Vector Machine (SVM) is a machine learning algorithm based on the Statistical Learning Theory (SLT), which can get good classification effects with a fe