Progressive failure analyses results are presented for composite curved panels and cylinders with cutouts and subjected to axial compression load.Three-dimensional Hashin failure criteria and Ye failure criteria were adopted as material damage initiation criteria for fiber failure, matrix failure and delamination failure that arise in composite laminates, and nonlinear material degradation scheme based on CDM (Continuum Damage Mechanics) was applied to simulate the damage evolution.