Shougang Group has developed advanced high-strength wear-resistance steel of NM450 by using Nb-Mo-Cr-Ti-B micro-alloyed design and two-stage rolling and quenching and tempering process.In spite of hig
【机 构】
：
Shougang Research Institute of Technology,No.69,Yangzhuang Street,Shijingshan District,Beijing China
论文部分内容阅读
Shougang Group has developed advanced high-strength wear-resistance steel of NM450 by using Nb-Mo-Cr-Ti-B micro-alloyed design and two-stage rolling and quenching and tempering process.In spite of high strength,the toughness and weldability of the steel was improved by reducing the carbon equivalent.For the high-strength wear-resistant steel,the yield strength is higher than 1100MPa,the tensile strength is higher than 1350MPa,the elongation is greater than 15%,the low temperature(-40℃)impact energy value is not less than 60J,and the Brinell hardness value of surface is more than 430HB.The abrasion resistance of NM450 is five times of that of the Q235.The high-strength wear-resistance steel is successfully applied in Shougang SGE150(R)heavy dump body to replace the plain carbon steel Q235,resulting in the reduction of body weight,the improvement of the life of the mine car and the reduction of the transportation costs.
其他文献
Potential benefits of vanadium in heat treated medium carbon bar steels are considered by reviewing examples from several recent studies.Emphasis is placed on microstructural development,strength,and
An new method is proposed to predict in sequence the phase transformation behavior and the depth of the decarburized ferrite layer with simultaneous scaling of a steel during cooling process from the
We introduce a new strengthening heat treatment of a Ni-Cr-Mo-V alloyed spring steel by partial isothermal salt-bath and subsequent air-cooling and tempering.Detailed isothermal treatments were made a
690MPa high strength steel with low yield ratio for building structure has been developed successfully by micro-alloying design and thermal-mechanical controlled processing in WISCO.The mechanical pro
In the shipbuilding industry,the welding efficiency of the ship plate not only has a great effect on the construction cost of the ship,but also affects the construction speed and determines the delive
In multi-pass welding process,various thermal cycle of both weld metal(WM)and heat affected zone(HAZ)will be subjected several times.This will make the initial microstructure occur an irreversible tra
Effect of heat-affected zone(HAZ)on spot weldability in automotive hot stamping(HS)steel sheet was investigated for automotive applications.Tensile test was performed on a tensile testing machine at a
For the purpose of obtaining the optimal microstructures and mechanical properties of the CGHAZ under high input welding,continuous cooling transformation diagrams of the coarse grain heat-affected zo
Continuous cooling transformation diagrams and microstructures of coarse grain heat-affected zone(CGHAZ)of V-N-Ti and Nb-V-Ti microalloyed steels at different cooling time form 800℃ to 500℃(t8/5)were
Ultra-high strength steels are materials of considerable interest for automotive and structural applications and are increasingly being used in those areas.Higher strength,however,makes steels more pr