【摘 要】
：
We introduce a new strengthening heat treatment of a Ni-Cr-Mo-V alloyed spring steel by partial isothermal salt-bath and subsequent air-cooling and tempering.Detailed isothermal treatments were made a
【机 构】
：
Materials and Engineering Research Institute,Sheffield Hallam University,Howard Street,Sheffield,S1
论文部分内容阅读
We introduce a new strengthening heat treatment of a Ni-Cr-Mo-V alloyed spring steel by partial isothermal salt-bath and subsequent air-cooling and tempering.Detailed isothermal treatments were made at temperatures below or above the Ms point(230℃).The salt bath time was controlled between 10 and 80 minutes.Through the new treatment,the candidate steel developed ultrahigh tensile strength~2,100 MPa,yield strength~1,800 MPa,elongation 8-10%,hardness 580-710 HV,and V-notch Charpy toughness 10-12 J.Optical and electron microscopic observations and X-ray diffraction revealed multi-phase microstructures of bainitic/martensitic ferrites,fine carbide precipitates and retained austenite.Carbon partitioning during the bainitic/martensitic transformation was investigated for its remarkable influence on the strengthening mechanism.
其他文献
Microstructure evolution during hot rolling depends on several processing variables.These are the furnace soaking temperature and,for each pass in the schedule,the temperatures,the strains,the strain
Vanadium microalloying is highly effective in high strength strip steels produced by thin slab casting and direct rolled process.Because of the high solubility of V(C,N)in austenite,vanadium is likely
The flow stress under typical hot coiling conditions has been quantified for low C and Nb-Ti(V)microalloyed steels.The equation is intended for calculating the amount of bending torque required during
Ultra-fast cooling(UFC)has been increasingly applied in industry,but accompanying with great changes of rolling strategy.It is therefore of importance to evaluate the characteristics of steels produce
The differences of microstructure and property of non-quenched and tempered bainitic steel under different finish rolling temperatures was analyzed by the methods of color metallographic,scanning elec
Before being subjected to water quenched,16mm WDL690D steel was heated at 910℃,930℃,950℃and 970℃for 20min,40min and 60min,respectively.Microstructures of these samples after heat treatment were observ
A new V-Ti-Mo complex micro-alloyed hot-rolled high strength sheet steel was developed by controlling a thermomechanical controlled processing(TMCP)schedule,in particular with variants in coiling temp
To develop thickness>60mm,yield strength>550MPa high-strength steel plate,the effects of heat treatment process on the microstructure and mechanical properties of plate specimens were investigated on
Potential benefits of vanadium in heat treated medium carbon bar steels are considered by reviewing examples from several recent studies.Emphasis is placed on microstructural development,strength,and
An new method is proposed to predict in sequence the phase transformation behavior and the depth of the decarburized ferrite layer with simultaneous scaling of a steel during cooling process from the