【摘 要】
：
In the present work, flexible porous carbon nanofibers (PCNFs) of 215 nm diameter were prepared by electrospinning process using resole-type liquefied phenolic resin (RLPR) as precursor.The addition o
【机 构】
：
College of Materials Science and Engineering, Northeast Forestry University, Harbin 150040,China;Eng
论文部分内容阅读
In the present work, flexible porous carbon nanofibers (PCNFs) of 215 nm diameter were prepared by electrospinning process using resole-type liquefied phenolic resin (RLPR) as precursor.The addition of defined amount of polyvinyl alcohol (PVA) is essential for the bead-free fibers forming.The final PCNFs were obtained after one-step carbonization of as-spun nanofibers,Which presented abundant micropores (0.9 nm and 1.8 nm) and high specific surface area of 956 m2/g without any activation process.This indicates that the flexible RLPR-based PCNFs will be promising not only in adsorbent and catalyst support materials but also as materials in electrode capacitance application.
其他文献
利用TGA以及固定床裂解器对生物质催化裂解特性进行研究,讨论CaO以及ZSM-5二元催化裂解对生物质的热裂解特性、芳烃含量以及选择性的影响,结果表明:断键催化剂CaO以及脱氧ZSM-5催化剂的加入改变了生物质的热解特性,致使残炭率明显增加,最大失重速率降低,生物质的转化率增加,催化剂的活性大小顺序为:ZSM-5＞CaO+ZSM-5＞CaO＞生物质,同时,催化剂的添加使其特性参数(活化能:Ea、活化
本文主要综述了双金属催化剂的制备方法对催化剂形貌、结构、催化性能的影响到双金属催化剂研究进展和应用领域,在将来对高利用率高活性催化剂研究的展望.浸渍法工艺生产流程简单,生产能力高以及金属活性组分利用率高,成本低廉,但存在颗粒分布不均匀导致金属活性组分分布不均匀,使其催化活性降低.沉淀法、溶胶-凝胶法和置换法拥有稳定性高的催化活性.电沉积法可在各种结构复杂的载体上均匀沉积,还可通过电流来控制沉积速度
Biodiesel was prepared from rubber seed oil catalyzed by phosphotungstic acid (HPW)based mesoporous silica prepared by direct method.The optimum biodiesel synthesis conditions were studied versus vari
在不同浓度的NaOH溶液中处理ZSM-5,将其应用在小桐子油催化裂化反应中以考察其催化性能,采用XRD、BET及SEM三种表征手段,对不同浓度NaOH碱液处理后的ZSM-5(硅铝比25∶1)进行调控其结晶度与孔道结构的研究.结果表明,碱处理能够扩大ZSM-5中的孔隙,提高介孔的数量以及比表面积.在装填1.0mol/L NaOH处理过后的分子筛,反应温度为550℃,质量空速12.21h-1,取得最佳
本试验主要研究了超声波辅助水酶法提取核桃油的酶解工艺.在中性蛋白酶的作用下,研究了酶解温度、酶的添加量、固液比、超声时间对油脂提取率的影响.结果表明在酶解温度60℃,蛋白酶添加量为2.5％(m/m),料液比1∶5,超声酶解时间为60min的条件下,核桃油的提取率可达到50％左右.
本研究通过氨水沉淀、Na2CO3浸渍、焙烧等处理步骤制备了负载型固体碱Na2O/Al2O3-MgO催化剂.借助XRD、BET、SEM分析发现,催化剂前体具有类水滑石结构,该前体经焙烧处理后,所得催化剂比表面积为105m2/g,其成分除Al2O3、MgO外,还存在Na-Al及Na-Al-Mg氧化物.将Na2O/Al2O3-MgO催化剂应用于蒜头果油甲酯化过程中,通过单因素试验及正交试验,并在综合考虑
优选一步法合成的紫茎泽兰厌氧发酵残留物固体酸为催化剂,考察其催化酸化小桐子油的酯化反应效果.着重考察醇油摩尔比、催化剂用量、反应时间、反应温度等因素的影响.试验结果表明,紫茎泽兰厌氧发酵残留物炭基固体酸可显著提高酯化反应效率,在醇油摩尔比为8∶1、催化剂用量为4％、反应温度为80℃和反应时间2h的反应条件下,转化率可达76.32％.试验提供了紫茎泽兰综合利用的新方法,具有良好的应用前景.
本试验以小桐子油为原料,在实验室的小型模拟固定床装置中,探究了不同催化剂、温度、质量空速对小桐子油催化裂解效果的影响.开展植物油脂催化裂化的研究,以降低能耗,并获得较好品质的燃料油,具有重要的意义.本文以小桐子油为代表,进行油脂的催化裂化实验条件的探究,以期为该类反应提供参考.
以麻疯树油为原料、Pt/SAPO-11为催化剂,一步加氢催化制生物航空煤油;在高压微型固定床反应器上研究了温度、压力、氢油比和空速等条件对Pt/SAPO-11催化麻疯树油一步加氢制生物航空煤油过程中脱氧率、C8～C16烃的选择性以及C8～C16烃异构率的影响.结果表明:在温度390℃、压力5MPa、氢油比1000、空速1.2h-1的最佳实验条件,脱氧率为98.13％,C8～C16烃的选择性为45.
以小桐子油为原料,在负载Pt的催化剂上一步加氢制备生物航空煤油.探究了反应温度,氢压,油剂比,反应时间和搅拌转速对C8～C16烃的比率和C8～C16烃异构率的影响,结果表明:最佳反应条件为反应温度为290℃,氢压为2.5MPa,油剂比为10∶1,反应时间为3h,反应转速为200rpm,在该条件下产物C8～16烃的比率为69.2％,C8～C16烃的异构率为19.01％,对精馏后的产品进行了理化性质检