【摘 要】
：
SiO2 antireflective films were prepared by sol-gel process with the precursor of tetraethylorthosilicate (TEOS).Polyethylene glycol (PEG, the average molecular weight is 400) was used in the sol proce
【机 构】
：
Shanghai Key Laboratory of Special Microstructure and Technology, Tongji University, Shanghai 200092
【出 处】
：
The 24th International Conference on Glass( ICG Congress 201
论文部分内容阅读
SiO2 antireflective films were prepared by sol-gel process with the precursor of tetraethylorthosilicate (TEOS).Polyethylene glycol (PEG, the average molecular weight is 400) was used in the sol process to control the growth process of particles to obtain films with different optical properties.
其他文献
Nonlinear optical fibers with the functionalities of light processing are very promising building blocks in signal modulating, routing and switching in fiber network system.The fabrication of second o
yb3+-doped fluorophosphate core and phosphate double-cladding heterogeneous fiber preform was prepared by the stacking method.The core, inner and outer cladding glasses were well matched in optical an
Ultrabroadband supercontinuum has received considerable attention due to its numerous applications in practice.An ultrabroadband supercontinuum spanning from 426 to 2954 nm is generated numerically in
Chalcogenide glass fibers are excellent candidates for broadband supercontinuum (SC) generation due to their excellent MIR transparency and high third-order nonlinearity.
A large-size (5 mm) yb3+-doped silica fibre core-glass rod with Al, Al-P, Al-F, or Al-P-F co-doped can be prepared by the sol-gel method combined with high-temperature melting technology12).We success
Fluorotellurite glass have attracted much attention for their potential applications in mid-infrared fiber devices.They have relatively low phonon energy, 1-2) a broad transmission window of 0.4～6 μm,
Bioresorbable optical materials have raised high interest in the last decade, due to the development of new techniques for biosensing, cancer therapy (Photodynamic therapy, PDT) and Optogenetics.Indee
monolithic alumina aerogels were prepared by sol-gel method combined with the ethanol supercritical drying and modification technique using alumina tri-sec butoxide and hydrochloric acid as the precur
Rare Earth (RE) ions are very important for diverse technological application, as lasers, wavelength downconverters, lighting, etc.Nd3+ is one of the most studied ions due to its potential application
Erbium doped silicate glasses and fibers have proven to be well suited for a large panel of optical applications,such as lasers and signal amplifiers (EDFA) operating around 1.53μm.Moreover, Er3+ dope