【摘 要】
:
monolithic alumina aerogels were prepared by sol-gel method combined with the ethanol supercritical drying and modification technique using alumina tri-sec butoxide and hydrochloric acid as the precur
【机 构】
:
Pohl Institute of Solid State Physics, Tongji University, Shanghai 200092
【出 处】
:
The 24th International Conference on Glass( ICG Congress 201
论文部分内容阅读
monolithic alumina aerogels were prepared by sol-gel method combined with the ethanol supercritical drying and modification technique using alumina tri-sec butoxide and hydrochloric acid as the precursor and catalyzer respectively.
其他文献
Optical fibers are now proving to have important roles in applications beyond telecommunications, such as sensing, biomedicine, defense, security and the development of novel light sources.
For Nd3+/Yb3+ co-doped material, lots of researches focus on Nd3+→Yb3+ energy forward-transfer (EFT), and the relevant spectroscopic and laser results have been reported.Recently, a novel phenomenon i
Ordered fiber bundles (FBs) operating in the mid-infrared spectral region are desirable for the collection and delivery of thermal images in extreme (e.g.under nuclear irradiation) or unfavorable envi
Nonlinear optical fibers with the functionalities of light processing are very promising building blocks in signal modulating, routing and switching in fiber network system.The fabrication of second o
yb3+-doped fluorophosphate core and phosphate double-cladding heterogeneous fiber preform was prepared by the stacking method.The core, inner and outer cladding glasses were well matched in optical an
Ultrabroadband supercontinuum has received considerable attention due to its numerous applications in practice.An ultrabroadband supercontinuum spanning from 426 to 2954 nm is generated numerically in
Chalcogenide glass fibers are excellent candidates for broadband supercontinuum (SC) generation due to their excellent MIR transparency and high third-order nonlinearity.
A large-size (5 mm) yb3+-doped silica fibre core-glass rod with Al, Al-P, Al-F, or Al-P-F co-doped can be prepared by the sol-gel method combined with high-temperature melting technology12).We success
Fluorotellurite glass have attracted much attention for their potential applications in mid-infrared fiber devices.They have relatively low phonon energy, 1-2) a broad transmission window of 0.4~6 μm,
Bioresorbable optical materials have raised high interest in the last decade, due to the development of new techniques for biosensing, cancer therapy (Photodynamic therapy, PDT) and Optogenetics.Indee