利用超重力富集高炉碳化渣中TiC的研究
【摘 要】
：
攀钢碳化渣中有价组元碳化钛晶粒细小，且弥散地分布在炉渣的多种矿相中，常规选矿分离技术很难将碳化钛从碳化渣中有效富集出来。本论文将超重力场引入碳化渣中碳化钛的富集提取中，重点探讨了碳化渣在等温条件不同重力系数与不同时间下碳化钛的富集规律。
【机 构】
：
冶金与生态工程学院,北京科技大学,北京,100083;钢铁冶金新技术国家重点实验室,北京科技大学,北京,100083
【出 处】
：
2016年全国冶金物理化学学术会议
【发表日期】
：
2016年10期
其他文献
The polypyrrole(PPY)has a broad application as a kind of conducting polymer with good physical and chemical properties,and it has been researched extensively in the field of metal corrosion and protec
会议
Super-hydrophobic Film Fabricated on Copper Surface as a Barrier against Marine Environmental Corros
In the marine environment,salt particles are easily absorbed on the surface of metals.With the role of humid air,it is prone to deliquesce to form a salt droplets remaining on the metal surface to for
会议
Microstructure and Corrosion Properties of CP-Ti and Ti-6Al-4V made by additive manufacturing method
Titanium and its alloys have been used in aerospace,marine,biological material industry,and various industries because of an excellent corrosion resistance and relatively low density and high specific
会议
The effects of isolated marine Pseudoalteromonas sp.on the stress corrosion behavior of duplex stainless steel were investigated by open circuit potential(OCP),potentiodynamic polarization curve,elect
会议
The microstructure and corrosion resistance of carbon film with different electronic structures formed on aluminum alloys was investigated by scanning electron microscopy and electrochemical workstati
会议
Biological elements have significant impact on lifetime prediction of marine carbon steel facilities.Microbe can produce pitting,crevice corrosion,selective dealloying and stress-oriented hydrogen-ind
会议
Molten salt reactors(MSR)is one of the most potential Generation IV reactors with high thermal efficiency and low primary system pressure.Molten salt have been used extensively in MSR as heat transpor
会议
Enhanced corrosion resistance of thermally-sprayed Fe-based amorphous coatings by eliminating Cr dep
Fe-based amorphous alloys draw much attention due to their excellent mechanical properties and corrosion resistance.Anti-corrosion coatings are one of the most prospective applications of Fe-based amo
会议
钙化焙烧是一种相对比较清洁的提钒工艺,实验考察了欠氧化焙烧下,焙烧温度、焙烧时间以及钙钒摩尔比对转炉钒渣酸浸过程中钒、铬浸出率的影响,并通过X 射线衍射,SEM 等检测方法对不同焙烧温度下转炉钒渣熟料的晶型和形貌进行了分析.实验结果表明,焙烧温度650℃,焙烧时间2 h,钙钒摩尔比0.55 时,焙烧熟料的钒浸出率达到89.00％,铬的浸出率达到12.64％.另外,适当提高焙烧温度有利于低价钒的氧化
本文研究了钒钛磁铁矿直接还原——熔分流程所得熔分钛渣的结晶行为,探索钛元素在渣中的富集特征。研究结果表明,通过调控熔分钛渣的化学组成,可使渣中析出黑钛石作为富钛相,其中,MgO 是促进黑钛石析晶的关键组分。黑钛石相呈长柱体状,晶粒尺寸可达几十至一百微米,且在适当提高熔分钛渣碱度的情况下易于通过磨矿实现单体解离；同时,黑钛石相中TiO2 含量高,是熔分钛渣较理想的富钛相。以黑钛石作为富钛相实现熔分钛