【摘 要】
：
采用差示扫描量热仪(DSC),分析了X60管线钢在加热与冷却过程中的相变温度。结果表明:在冷却时DSC曲线上出现三个峰值,除先共析铁素体析出和珠光体转变外,还有铌或钒的碳化物
【机 构】
：
内蒙古科技大学材料与冶金学院,内蒙古包头市专利事务所,
论文部分内容阅读
采用差示扫描量热仪(DSC),分析了X60管线钢在加热与冷却过程中的相变温度。结果表明:在冷却时DSC曲线上出现三个峰值,除先共析铁素体析出和珠光体转变外,还有铌或钒的碳化物析出;相变温度随冷却速度的增大而降低;在加热至950℃时,DSC曲线上出现二个峰值,除先共析铁素体溶解和奥氏体转变外,没有明显的铌或钒的碳化物峰溶入奥氏体峰。
Differential scanning calorimetry (DSC) was used to analyze the phase transition temperature of X60 pipeline steel during heating and cooling. The results show that there are three peaks on the DSC curve during cooling. In addition to proeutectoid ferrite precipitation and pearlite transformation, carbides of niobium or vanadium precipitate; the transformation temperature decreases with the increase of cooling rate; When heated to 950 ℃, there are two peaks on the DSC curve. No obvious niobium or vanadium carbide peaks dissolve into the austenite peak, except for proeutectoid ferrite dissolution and austenite transformation.
其他文献
介绍了功能梯度材料的基本概念,综述了该材料的制备方法,提出了其发展方向。
The basic concept of functionally graded material is introduced. The preparation method
利用多相平衡计算软件Pandat及镁合金热力学数据库绘制出了Mg-Gd系合金、Mg-Y系合金的计算平衡相图。利用铆钉法制备了Mg-Gd扩散偶、Mg-Y扩散偶,并基于局部平衡原理,将其在40
介绍了钛合金的热变形行为的研究概况,对钛合金的热变形行为进行了总结。
The research status of thermal deformation behavior of titanium alloy is introduced, and th
在混合元素法激光立体成形(LSF)过程中,由于各种纯金属粉末或中间合金的密度、粒度不同,使得不同种的粉末输送性不同,即粉末离开送粉管后形成的粉末流的发散角,或粉斑直径不
以弹塑性体冲击接触过程中冲击脉冲的估算为研究目标,采用非线性阻尼弹簧接触模型模拟弹塑性材料的冲击与接触。以铝合金为研究对象,将数值计算结果与实验结果进行对比,发现
采用了一种方便快捷、无杂质污染的异常晶粒长大方法,以多晶铜为原材料,获取小尺寸单晶铜/大晶粒多晶铜。利用光学显微镜观察了室温压缩之后的多晶Cu块体材料的异常晶粒长大
采用人工海水对含有相同基本成分的C钢和添加了0.95%Cr元素的Cr钢进行120h的流动冲刷腐蚀试验。利用SEM和XRD等方法研究了Cr元素对普碳钢锈层的形貌、物相构成及相对含量的影
采用粉末冶金法制备了AlNiCrFexMo0.2CoCu(x=0.5、1.0、1.5、2.0)高熵合金,研究了Fe元素对该合金组织和性能的影响。对上述4种合金进行XRD分析,发现当x=0.5、1.0和1.5时,有BC
应用固体与分子经验电子理论(即余氏理论EET)分别计算了Cr溶入到奥氏体和马氏体中的价电子结构,从价电子结构层次分析了Cr在钢中的作用机理.结果表明:Cr溶入到奥氏体后晶胞内
以低碳贝氏体钢HQ785为实验材料,利用Gleeble-3500热/力模拟试验机进行不同单向外加拉应力下的相变试验,通过光学显微镜分析了奥氏体组织,并测试了相变后的维氏硬度。结果表