非晶合金Fe76.5-xCu1.0NbxSi13.5B9.0(x=1,3,5和7)的穆斯堡尔研究表明,Nb元素对非晶合金的磁有序温度Tc和磁超精细相互作用有很大的影响,随着Nb含量的增加,Tc减小,x=1,3,5时分别为655,597,525K;但当x=7时,出现了两个Tc分别为470和539K,由所计算的磁超精细场分布P(H)表明,最大几率处的内磁场Ho和平均内磁场<H>都随Nb含量的增加而减小,而分布的宽度△H则反之,并出现了磁超精细场分布P(H)的低场峰,且低场的几率也随之增大,这些结果表明了Nb元素使非晶体Fe-Fe间的平均磁相互作用减弱且在非晶体中富集。
Mossbauer studies of amorphous alloys Fe76.5-xCu1.0NbxSi13.5B9.0 (x = 1, 3, 5, and 7) have shown that the magnetic ordering temperature Tc and magnetic hyperfine mutuality of Nb for amorphous alloys Tc decreases with the increase of Nb content, which are respectively 655,597 and 525K at x = 1,3,5; however, when x = 7, there are two Tc values of 470 and 539K. From the calculated magnetic hyperfine field distribution P (H), it is shown that the internal magnetic field Ho and the average internal magnetic field at the maximum probability decrease with the increase of Nb content, while the distribution width ΔH, on the contrary, And the low field peak of magnetic superfine field distribution P (H) appears, and the probability of low field also increases. These results show that Nb element weakens the average magnetic interaction between amorphous Fe-Fe, Rich in crystals.